Microstructure and Mechanical Properties of Vacuum Laser Welded Joints in 42CrMo Thick Plate

Vacuum laser welding trials were carried out on 42CrMo steel, a material widely utilized in the defense sector. By employing a 30 kW fiber laser system, complete penetration welds were successfully produced on 20 mm thick 42CrMo steel plates. The resulting joints displayed satisfactory surface quality on both the top and bottom sides, with no evident defects such as cracks or porosity. A comprehensive analysis of the joint microstructure and mechanical properties was conducted. Findings reveal that the weld zone (WZ) is predominantly composed of lath martensite, accompanied by minor quantities of plate martensite, organized as columnar crystals. The joints demonstrated high tensile strength at ambient temperature, with fracture consistently occurring within the base metal (BM). Microhardness measurements indicated higher values within the weld relative to the base metal, and no pronounced softening was detected in the heat-affected zone (HAZ). Additionally, the joints exhibited commendable impact toughness, suggesting overall superior mechanical performance.