Investigation of Fatigue Lives of Spot Friction Welds in Lap-Shear Specimens of Aluminum 6111-T4 Sheets Based on Fracture Mechanics

The fatigue lives of spot friction welds in lap-shear specimens of aluminum 6111-T4 sheets are investigated here. The paths of fatigue cracks near spot friction welds are first discussed. A fatigue crack growth model based on the Paris law for crack propagation and the local stress intensity factors for kinked cracks is then adopted to predict the fatigue lives of spot friction welds. The global and local stress intensity factors based on a recent work of Wang and Pan for resistance spot welds in lap-shear specimens are used to estimate the local stress intensity factors of kinked cracks with experimentally determined kink angles. The results indicate that the fatigue life predictions based on the Paris law and the local stress intensity factors as functions of the kink length agree well with the experimental results.