Durability Study of Electronic-grade Glass Fibers in Salt-Alkali Environments

Electronic substrates and copper-clad laminates are widely used in modern life, particularly in electronic products such as coastal communication base stations and ship communication and navigation system. In these environments, salt particles carried by sea fog can adhere to the surface of the substrates along with moisture, leading to salt-alkali corrosion of the products. As a core material in electronic components, electronic-grade glass fiber urgently requires investigation into its durability under salt-alkali conditions. Therefore, this study focuses on a specific type of electronic-grade glass fiber and explores its corrosion behavior in three different environments: 2 mol/L NaOH, 1 mol/L cement solution, and 3.5 % NaCl. Soaking durations of 6, 12, 24 hours and 3, 7, and 14days were selected as key parameters. The mechanical properties and surface morphology of the fibers before and after corrosion were observed and analyzed. Experimental results indicate that the glass fiber exhibits higher durability in saline solutions than in alkaline environments. This study provides theoretical support for evaluating the long-term performance of Electronic grade glass fibers in practical applications. It also contributes to the optimization of raw materials and manufacturing processes, enhancing the performance of such fibers in salt-alkali conditions, and offers valuable reference for future research on glass fiber-reinforced composites.