Anticorrosion of Painted Galvanized Steel in Relation with Physical Properties of the Paint Film
Annotation ability available
Sector:
Language:
English
Abstract
In order to elucidate the anticorrosion properties of painted Galvan-nealed Steel(GA) in relation with physicochemical properties of paint films such as adhesion, anticorrosion performance of the painted GA was examined by natural weathering along with artificial corrosion tests and the following results were obtained.
- 1. In the filiform corrosion and natural weathering test, anticorrosive performances of painted GA are superior to painted cold rolled steel (CR).However, the GA was inferior to the latter in the salt fog test and the wet adhesion test.
- 2. In the filiform corrosion, the natural weathering and the wet adhesion test, the stress relaxation, adhesion as well as the barrier effect of paint films are very important to the anti-corrosion performance.
- 3. In salt fog test, the resistivity against permeaton is the decisive factor to the corrosion preventive properties.
Also, the effect is more pronounced with GA than with CR.
Recommended Content
| Technical Paper | Lead Free Cationic Electro-Deposition for Automobile Body in White |
| Technical Paper | The Autodeposition of Coatings on Galvanized Substrates |
Authors
Citation
Satoh, T. and Nobutoh, K., "Anticorrosion of Painted Galvanized Steel in Relation with Physical Properties of the Paint Film," SAE Technical Paper 860111, 1986, https://doi.org/10.4271/860111.Also In
References
- Leidheiser, H. Jr Corrosion-NACE 38 8 July 375 1981
- Satoh Yasushi J. Jpn. Soc. Colour Material 54 6 379 1981
- Funke W. JOCCA 62 63 1979
- Mayne J. O. Official Digest 24 127 1952
- Satoh Tadaaki Kogure Hideo Nakatani Aisaku J. Jpn. Soc. Colour Material 54 6 333 1981
- Satoh Tadaaki Kogure Hideo Nakatogawa Yumi Coating Technology 18 8 307 1983
- Kogure Hideo Satoh Tadaaki Imai Takeo Transaction ISJI 23 1010 1983
- Ishihara Shigetoshi Transaction ISJI 23 897 1981
- Nakagawa T. Kobunshi 17 1181 1981
- Maeda S. Asai T. et al 9th Inter. Conf. Organic Coating and Technology 1983 Athen
- Saitoh Takao et al Testuto-Hagane 70 5 463 1984
- Pourbyix Marcel “Atlas of electrochemical equibria in aqueous solution” NACE 1974
- Nobutoh Kenichi