Paint Bake Influence on AA7075 and AA7085
Technical Paper
2017-01-1265
ISSN: 0148-7191, e-ISSN: 2688-3627
This content contains downloadable datasets
Annotation ability available
Sector:
Language:
English
Abstract
The typical paint bake cycle includes multiple ramps and dwells of temperature through e-coat, paint, and clear coat with exposure equivalent to approximately 190°C for up to 60 minutes. 7xxx-series aluminum alloys are heat treatable, additional thermal exposure such as a paint bake cycle could alter the material properties. Therefore, this study investigates the response of three 7xxx-series aluminum alloys with respect to conductivity, hardness, and yield strength when exposed to three oven curing cycles of a typical automotive paint operation. The results have indicated that alloy composition and artificial aging practice influence the material response to the various paint bake cycles.
Recommended Content
Journal Article | Stress-Corrosion Cracking Evaluation of Hot-Stamped AA7075-T6 B-Pillars |
Aerospace Material Specification | Cleaner for Aircraft Exterior Surfaces Wipe-On, Wipe-Off, Containing Suspended Abrasive Solids |
Aerospace Material Specification | Cleaner for Aircraft Exterior Surfaces Wipe-On, Wife-Off |
Authors
Citation
Harrison, N., Luckey, S., Cappuccilli, B., and Kridli, G., "Paint Bake Influence on AA7075 and AA7085," SAE Technical Paper 2017-01-1265, 2017, https://doi.org/10.4271/2017-01-1265.Data Sets - Support Documents
Title | Description | Download |
---|---|---|
Unnamed Dataset 1 | ||
Unnamed Dataset 2 | ||
Unnamed Dataset 3 |
Also In
References
- Harrison , Nia , and Luckey S. George Artificial Aging Process For High Strength Aluminum. Ford Global Technologies, LLC, assignee 20150101718 16 Oct 2013
- Vasudevan , A. K. , and Doherty R.D. Aluminum Alloys-contemporary Research and Applications Boston Academic 1989 www.Google.University of Virginia.Web 27 July 2016
- Physical Metallurgy and Processes 2003 Handbook of Aluminum 1
- Regional Heat Curve Cycles for Adhesives, Deadeners, Foams, and Sealers 2010 Ford Laboratory Test Method 150 05
- Mechanical Properties Measurement after Thermal Processing of Aluminum Alloy Sheet 2016 Ford Laboratory Test Method 107 01
- United States Department of Defense 1991 Heat Treatment of Aluminum Alloys
- ASTM B918/B918M-09 Standard Practice for Heat Treatment of Wrought Aluminum Alloys ASTM International West Conshocken, PA www.astm.org
- The Effects of Natural Aging and Solution Heat Treatment Times on AA7075 Aluminum Alloys Ford Motor Company Technical Report
- Aluminum Alloy Characterization of Hardness and Yield Strength Ford Motor Company Technical Report