Fatigue Behavior of Stainless Steel Sheet Specimens at Extremely High Temperatures

SAE 2014 World Congress & Exhibition
Authors Abstract
Active regeneration systems for cleaning diesel exhaust can operate at extremely high temperatures up to 1000°C. The extremely high temperatures create a unique challenge for the design of regeneration structural components near their melting temperatures. In this paper, the preparation of the sheet specimens and the test set-up based on induction heating for sheet specimens are first presented. Tensile test data at room temperature, 500, 700, 900 and 1100°C are then presented. The yield strength and tensile strength were observed to decrease with decreasing strain rate in tests conducted at 900 and 1100°C but no strain rate dependence was observed in the elastic properties for tests conducted below 900°C. The stress-life relations for under cyclic loading at 700 and 1100°C with and without hold time are then investigated. The fatigue test data show that the hold time at the maximum stress strongly affects the stress-life relation at high temperatures. When the results are plotted as functions of the time to failure, the test data suggest that creep dominates the failure of the sheet specimens at elevated temperatures.
Meta TagsDetails
Avery, K., Pan, J., Engler-Pinto, C., Wei, Z. et al., "Fatigue Behavior of Stainless Steel Sheet Specimens at Extremely High Temperatures," SAE Int. J. Mater. Manf. 7(3):560-566, 2014, https://doi.org/10.4271/2014-01-0975.
Additional Details
Apr 1, 2014
Product Code
Content Type
Journal Article