High Temperature Properties of Magnesium Die Casting Alloys
Annotation ability available
Sector:
Language:
English
Abstract
The development of magnesium for components which must withstand appreciable loads at elevated temperatures must be accompanied by an expanded material properties database. Tensile, creep and stress relaxation properties are among those particularly needed to provide automotive product engineers with proper information to design in magnesium. This paper provides a compilation to date of property data which are being generated in ongoing research and development programs. Magnesium alloys from the AE and AS series are particularly emphasized.
Recommended Content
Authors
Citation
Aune, T. and Ruden, T., "High Temperature Properties of Magnesium Die Casting Alloys," SAE Technical Paper 920070, 1992, https://doi.org/10.4271/920070.Also In
References
- “Standard Methods of Tension Testing Wrought and Cast Aluminum and Magnesium Alloy Products” ASTM B557M, 1990 Annual Book of ASTM Standards 02 02
- Norsk Hydro Internal Report RP91.AR9 August 1991
- Norsk Hydro Internal Report RP91.AV7 September 1991
- Smith, W.F. “Principles of Materials Science and Engineering,” 288 291 McGraw Hill 1986
- “Recommended Practice for Conducting Creep, Creep Rupture, and Stress-Rupture Tests of Metallic Materials” ASTM E139, 1990 Annual Book of ASTM Standards 03 01
- Miller, W. K. “Creep of Die Cast AZ91 Magnesium at Room Temperature and Low Stress” Metallurgical Transactions A 22A 873 877 April 1991
- Aune, T. Kr. Albright, D. L. “Stress Relaxation Behavior of Die Casting Alloys” SAE Paper 910412 Society of Automotive Engineers 1991
- Cameron, T.B. “Use of Threaded Fasteners in Die Cast Magnesium” SAE Paper 860289 Society of Automotive Engineers 1986
- “Standard Recommended Practices for Stress Relaxation Tests for Materials and Structures” ASTM E328, 1990 Annual Book of ASTM Standards 03 01
- “Standard Relaxation Testing” Metals Handbook 9th 8 322 American Society for Metals 1985