Predicting Yield Strength and Tensile Strength After Forming for Automotive Integral Body Structural Rail Type Parts
Annotation ability available
Sector:
Language:
English
Abstract
Samples of cold rolled and hot dip galvanized mild steel, microalloyed high strength steel, and dual phase steel were prestrained by bending and straightening, bending and straightening with superimposed tensile strain in a die, and cold rolling (dual phase steels only). In all three cases, the strain state was approximately plane strain. Stress-strain behavior was evaluated by conventional tensile testing of as-received and prestrained samples. For the mild and the high strength microalloyed steels, it is shown that the use of effective prestrain calculated assuming isotropy coupled with simple parabolic work hardening provides reasonable engineering estimates of the yield and tensile strength after prestraining if κ and n are taken from as-received tensile tests oriented coaxially to the restrain direction. It was also found that in bending and straightening, only the absolute average value of the bending strain should be used in calculating the effective prestrain. For steels with dual phase microstructures, this approach to predicting cold work strengthening does not provide useful engineering estimates.
Recommended Content
Technical Paper | Experimental Investigation of Springback of Dual-Phase Steels |
Technical Paper | Automotive Applications of Stretch Flange High Strength Steel |
Ground Vehicle Standard | Properties of Galvanized Low Carbon Sheet Steels and Their relation to Formability |
Authors
Topic
Citation
Levy, B., "Predicting Yield Strength and Tensile Strength After Forming for Automotive Integral Body Structural Rail Type Parts," SAE Technical Paper 840009, 1984, https://doi.org/10.4271/840009.Also In
References
- Laukonis J. V. Met, Trans. A 12A March 1981 467
- Wagoner R. H. Laukonis J. V. Met. Trans. A 14A July 1983 1487
- Laukonis J. V. Ghosh A. K. Met. Trans. A 9A December 1978 1849
- Garofalo F. Low, J. R. Jr. J. of Mech. and Phys. of Solids 8 1955 275
- Dieter, G. E. Jr. Mechanical Metallurgy McGraw Hill 1st Edition 1961 66
- Vecchio M. T. SAE 830398 February 28-March 4 1983
- Nine H. D. J. of Appl. Metalworking July 1982 2 3 200