Effect of Fiber Length on the Mechanical Properties of Woven Jute/Raw Sisal Fiber Composite
Technical Paper
2020-28-0417
ISSN: 0148-7191, e-ISSN: 2688-3627
This content contains downloadable datasets
Annotation ability available
Sector:
Language:
English
Abstract
The use of natural fibers composite matrix is tremendously increasing day to day and acting as a replacement product to many conventional materials in the automobile and aviation sectors. It was preferred due to its bio-degradability, weight to strength ratio, easy availability, and lightweight. The crisscrossed woven jute and raw-sisal fibers had drawn the superior properties in the advanced developing field of the composite. The main purpose of this project is to evaluate the mechanical properties and the influence of raw sisal fiber with woven Jute/Epoxy composite by varying the size of raw sisal in three variable lengths such as 10mm, 20mm, and 30mm respectively. The composite laminates were fabricated by the conventional hand-layer technique. The mechanical characterization like the tensile test, flexural test, and hardness, was estimated on the fabricated jute/sisal hybrid composite material. It was observed that the S3 (30mm fiber length) composite had shown 22MPa tensile strength and 3.6GPA of tensile modulus than the other composites. The S3 composite was obtained better impact strength of 1.95J than the S1 and S2 composites. The work was not only explaining the properties of crisscross has woven jute and raw sisal fiber but also suggests innovation in implementing the structural stabilized product in automobile industries.
Recommended Content
Authors
- Harsha Vardhan Reddy - Vellore Inst of Technology
- S.V Bharath Reddy - Vellore Institute of Technology Vellore
- N.Sasikiran Reddy - Vellore Institute of Technology Vellore
- Rajamurugan Govindasamy - Vellore Inst of Technology
- Prabu Krishnasamy - Vellore Institute of Technology,Vellore
- Quberk jeeva singh C - Vellore Institute of Technology,Vellore
Topic
Citation
Vardhan Reddy, H., Reddy, S., Reddy, N., Govindasamy, R. et al., "Effect of Fiber Length on the Mechanical Properties of Woven Jute/Raw Sisal Fiber Composite," SAE Technical Paper 2020-28-0417, 2020, https://doi.org/10.4271/2020-28-0417.Data Sets - Support Documents
Title | Description | Download |
---|---|---|
Unnamed Dataset 1 | ||
Unnamed Dataset 2 | ||
Unnamed Dataset 3 | ||
Unnamed Dataset 4 | ||
Unnamed Dataset 5 |
Also In
References
- Boopalan , M. , Umapathy , M.J. , and Jenyfer , P. 2012
- Bragaa , R.A. and Magalhaes Jr , P.A.A. 2015
- Samanta , S. , Muralidhar , M. , Jackson Singh , T. , and Sarkar , S.
- Jawaid , M. , Abdul Khalil , H.P.S. , Hassan , A. , and Dungani , R. 2012
- Adhikari , R.K. and Keerthi Gowda , B.S.
- Saha , K. , Das , S. , Bhatta , D. , and Mitra , C. 1998
- Sreekumar , P.A. , Selvin , P. Thomas , J.M.S. , Joseph , K. et al. 2009
- Zhao , X. , Li , R.K.Y. , and Bai , S.L. 2014
- Milanese , A.C. , Cioffi , M.O.H. , and Voorwald , H.J.C. 2012
- Bakare , I.O. , Okieimen , F.E. , Pavithran , C. , Abdul Khalil , H.P.S. et al. 2010
- Ratna Prasad , A.V. and MohanaRao , K. 2011
- Mishra , V. and Biswas , S.
- Arulmurugan , M. , Selvakumar , A.S. , Prabu , K. , and Rajamurugan , G. Effect of Barium Sulphate on Mechanical, DMA and Thermal Behaviour of Woven Aloevera/Flax Hybrid Composites Bull. Mater. Sci. 43 1 1 10 2020 https://doi.org/10.1007/s12034-019-2018-7
- Prabu , K. , Rajamurugan , G. , and Thirumurugan , M. Dynamic Mechanical Analysis of 304 Wire Mesh Reinforced Hybrid Jute Fiber/Epoxy Composite J Ind Text 2019 https://doi.org/10.1177/1528083719883057
- Arulmurugan , M. , Prabu , K. , Rajamurugan , G. , and Selvakumar , A.S. Impact of BaSO4 Filler on Woven Aloevera/Hemp Hybrid Composite: Dynamic Mechanical Analysis Material Research Express 6 1 13 2019 https://doi.org/10.1088/2053-1591/aafb88