Bending Fatigue and Microstructure of Fillet Welded Joints with High Chromium Stainless Pipe for Catalyst Muffler
Technical Paper
2017-01-0472
ISSN: 0148-7191, e-ISSN: 2688-3627
This content contains downloadable datasets
Annotation ability available
Sector:
Language:
English
Abstract
To prevent corrosion of the inlet part with aqueous ammonia injection, high chromium corrosion-resistant materials have been applied for welded joints of mufflers. Bending fatigue strength of welded joint samples of flange pipes was defined through fatigue experiments, modeling that high fluctuating stresses exist in the inlet and outlet flange pipes of a muffler caused by the vibration of a moving vehicle. Factors that caused fatigue to failure such as welding bead shape and metallographic structure were identified through local stress measurements, FEM stress simulations, microscopic observations, and SEM-EDS composition analyses. By comparing with sample A having a smaller flank angle and sample B having a larger flank angle, the results suggested that the difference of bending fatigue strengths at 200,000 cycles was 24% when based on nominal stress, and the difference was 10% when based on measured maximum stress. The maximum stress was inversely proportional to weld flank angle non-linearly. The crack starting point of sample A was at weld interface, a boundary between weld acicular phase and pipe ferrite phase, but that of the sample B was not at the boundary between weld lathy phase and pipe ferrite phase. After etching with strong mixed acids, the sensitization in grain boundary occurred in the 17Cr flanges, but it did not occur in the 30Cr pipes.
Recommended Content
Authors
Citation
Oh, G., "Bending Fatigue and Microstructure of Fillet Welded Joints with High Chromium Stainless Pipe for Catalyst Muffler," SAE Technical Paper 2017-01-0472, 2017, https://doi.org/10.4271/2017-01-0472.Data Sets - Support Documents
Title | Description | Download |
---|---|---|
Unnamed Dataset 1 | ||
Unnamed Dataset 2 | ||
Unnamed Dataset 3 |
Also In
References
- Xiaoguang Wang (Gyoko Oh) et al. Fatigue and microstructure of welded joints of metal sheets for automotive exhaust system JSAE Review 24 3 295 301 2003
- Xiaoguang Wang (Gyoko Oh) et al. Synthesis of Co-Al composite oxides and catalytic activities for selective reduction of NO Shokubai (Catalysts & Catalysis) 42 2 130 132 2000
- Gyoko Oh Catalyst mufflers Publication of Patent Application 2003
- Smith , H. , Lauer , T. , Schimik , V. , and Gabel , K. Evaluation and Prediction of Deposit Severity in SCR Systems SAE Int. J. Engines 9 3 1735 1750 2016 10.4271/2016-01-0970
- Kazuyoshi Saida Weldability of stainless steels Journal of Japan Welding Society 79 6 40 50 2010
- Japan Society of Mechanical Engineers JSME mechanical engineers’ concise handbook 6th Maruzen 111 141 1990
- Japanese Industrial Standards Committee Methods of measurement for ferrite content in austenitic and austenitic-ferritic stainless steel deposited metals Japanese Industrial Standards 2006
- Missori S. et al. Laser beam welding of austenitic-ferritic transition joints Welding Research Supplement March 125 134 1997
- Hiroshige Inoue et al. Epitaxial growth and phase selection of austenitic stainless steel weld metals near fusion boundaries Quarterly Journal of the Japan Welding Society 15 2 281 291 1997
- Amuda M.O.H. et al. An overview of sensitization dynamics in ferritic stainless steel welds International Journal of Corrosion 2011 1 9 2011 10.1155/2011/305793