Creep Resistance of 2024 Aluminum Alloy
Technical Paper
2013-32-9110
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
Long term soaking creep rupture tests of a 2024 aluminum alloy in the T4 condition were performed at 100 °C and 130 °C under stresses ranged from 235 MPa to 370 MPa. It appears that the longer creep life can be obtained through the beneficial effect of underageing resulting in the GPB zones being retained in the matrix rather than dissolving and additional dynamic precipitation of S′ precipitates during testing; especially at the condition of 325 MPa at 100 °C, the alloy exhibits longer creep life of at least 14,604 h due to most fully developed very fine precipitates dispersion. When creep test at higher temperature (130°C), the grown S′ precipitates lead to significant reduction of creep rupture life. The correlation of applied stress, creep temperature, creep rupture time, and microstructure evolution were discussed.
Recommended Content
Technical Paper | Sheet Aluminum Wheels |
Technical Paper | Development of High-Temperature Coatings and Applications |
Aerospace Material Specification | Plating, Brush, Chromium Hard Deposit, Trivalent |
Citation
Wang, L. and Tsai, C., "Creep Resistance of 2024 Aluminum Alloy," SAE Technical Paper 2013-32-9110, 2013, https://doi.org/10.4271/2013-32-9110.Also In
References
- Muthu Kumaran , S. Identification of high temperature precipitation reactions in 2024 Al-Cu-Mg alloy through ultrasonic parameters Journal of Alloys and Compounds 539 0 179 183 2012
- Alfieri V. , Cardaropoli F. , Caiazzo F. , Sergi V. Investigation on Porosity Content in 2024 Aluminum Alloy Welding by Yb:YAG Disk Laser 383 - 390 Trans Tech Publications Switzerland 2011
- Wang , S. C. and Starink , M. J. Two types of S phase precipitates in Al-Cu-Mg alloys Acta Materialia 55 3 933 941 2007
- Khan I.N. , Starink Marco J. A Multi-Mechanistic Model for Precipitation Strengthening in Al-Cu-Mg Alloys during Non-Isothermal Heat Treatments 519-521 Trans Tech Publications Switzerland 2006
- Lumley , R. N. , Morton , A. J. , and Polmear , I. J. Enhanced creep performance in an Al-Cu-Mg-Ag alloy through underageing Acta Materialia 50 14 3597 3608 2002
- Lumley , R. N. and Polmear , I. J. The effect of long term creep exposure on the microstructure and properties of an underaged Al-Cu-Mg-Ag alloy Scripta Materialia 50 9 1227 1231 2004
- Wang , L.M. Microstructure and properties of certain 2000 series aluminium alloys PhD Imperial College London 1999
- Wang , L. M. , Flower , H. M. , and Lindley , T. C. Precipitation of the ω phase in 2024 and 2124 aluminium alloys Scripta Materialia 41 4 391 396 1999
- Polmear , I. J. and Couper , M. J. Design and development of an experimental wrought aluminum alloy for use at elevated temperatures Metallurgical Transactions A 19 4 1027 1035 1988
- Kloc , Luboš , Cerri , Emanuela , Spigarelli , Stefano , Evangelista , Enrico , and Langdon , Terence G. Significance of continuous precipitation during creep of a powder mettallurgy aluminum alloy Materials Science and Engineering: A 216 1-2 161 168 1996
- Kloc , L. , Spigarelli , S. , Cerri , E. , Evangelista , E. , and Langdon , T. G. Creep behavior of an aluminum 2024 alloy produced by powder metallurgy Acta Materialia 45 2 529 540 1997
- Li , Yong , Nutt , Steven R. , and Mohamed , Farghalli A. An investigation of creep and substructure formation in 2124 Al Acta Materialia 45 6 2607 2620 1997
- Mohamed , Farghalli A. Correlation between creep behavior in Al-based solid solution alloys and powder metallurgy Al alloys Materials Science and Engineering: A 245 2 242 256 1998
- Lin , Y. C. , Xia , Yu-Chi , Jiang , Yu-Qiang , and Li , Lei-Ting Precipitation in Al-Cu-Mg alloy during creep exposure Materials Science and Engineering: A 556 0 796 800 2012
- Lin , Y. C. , Xia , Yu-Chi , Ma , Xue-Song , Jiang , Yu-Qiang , and Chen , Ming-Song High-temperature creep behavior of Al-Cu-Mg alloy Materials Science and Engineering: A 550 0 125 130 2012
- Przydatek , J. The Elevated Temperature Deformation of Aluminium Alloy 2650 PhD thesis University of London London 1998
- Majimel , J. , Molénat , G. , Casanove , M. J. , Schuster , D. , Denquin , A. , and Lapasset , G. Investigation of the evolution of hardening precipitates during thermal exposure or creep of a 2650 aluminium alloy Scripta Materialia 46 2 113 119 2002
- Chen , Zhongwei , Chen , Pei , and Li , Shishun Effect of Ce addition on microstructure of Al 20 Cu 2 Mn 3 twin phase in an Al-Cu-Mn casting alloy Materials Science and Engineering: A 532 0 606 609 2012