Modeling and Simulation of Creep-Fatigue-Oxidation Crack Growth
Technical Paper
2013-01-0167
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
Creep, fatigue, oxidation, or their combinations are usually the fundamental underlying material degradation and failure mechanisms in advanced engines, manifolds, thermal regeneration systems, and other systems. Therefore, the basic understanding and appropriate mathematical modeling of these mechanisms are crucial in engineering designs. Several numerical simulation strategies are being pursued to achieve a long-term goal of virtual simulation of high-temperature degradation and failure of such components and systems.
In this paper, as the first step of the effort in virtual high-temperature material failure simulation, the numerical simulation of the recently developed crack growth models, i.e. creep-fatigue, fatigue-oxidation, and creep-fatigue-oxidation models, are conducted. It is demonstrated that the models developed can be implemented in an efficient way for virtual life assessment and engineering design applications.
Recommended Content
Authors
Citation
Wei, Z. and Yang, F., "Modeling and Simulation of Creep-Fatigue-Oxidation Crack Growth," SAE Technical Paper 2013-01-0167, 2013, https://doi.org/10.4271/2013-01-0167.Also In
References
- Saxena , A. , Dogan , B. Journal of ASTM International Selected Technical Papers, ASTM STP 1539 Creep-Fatigue Interactions: Test Methods and Models West Conshohocken, PA 2011
- Haigh , J.R. , Skelton , R.P. , Richards , C.E. Oxidation-assisted crack growth during high cycle fatigue of a 1% Cr-Mo-V steel at 500°C Materials Science and Engineering 1976 26 167 174
- Neu , R.W. , Sehitoglu , H. Thermomechanical fatigue, oxidation and creep: part I. Damage mechanisms Metal Trans 1989 20A 1755 81
- Neu , R.W. , Sehitoglu , H. Thermomechanical fatigue, oxidation and creep: part II. Life prediction Metal Trans 1989 20A 1755 81
- Reuchet , J. , Remy , L. Fatigue oxidation interaction in a superalloy-application to life prediction in high temperature low cycle fatigue Metallurgical Transactions A 1983 14 141 149
- Evans , J.L. Environment assisted crack growth in Ni-base superalloys at elevated temperature Ph.D thesis University of Arkansas Fayetteville, AR, USA 2008
- Findley , K.O. , Evans , J.L. , Saxena , A. A critical assessment of fatigue crack nucleation and growth models for Ni-and Ni, Fe-based superalloys International Materials Reviews 2011 56 49 71
- Wei , Z. , Yang , F. , Cheng , H. , Nikbin , K. Probabilistic prediction of crack growth based on creep/fatigue damage accumulation mechanism Journal of ASTM International 8 5 10.1520/JAI103690
- Wei , Z. , Yang , F. , Cheng , H. Oxidation assisted fatigue crack growth model and its probabilistic analysis the 17th ISSAT International Conference on Reliability & Quality in Design August 4 6 2011 Vancouver, B.C., Canada 1 5
- Wei , Z. , Yang , F. , Lin , B. , Luo , L. , Konson , D. , Nikbin , K. A new linear superposition theory and its application in creep-fatigue-oxidation crack growth modeling Proceedings of the ASME 2012 Pressure Vessels & Piping Division Conference July 15 19 2012 Toronto, Canada
- Tong , J. , Dalby , S. , Byrne , J. , Henderson , M.B. , Hardy , M.C. Creep, fatigue and oxidation in crack growth in advanced nickel base superalloys International Journal of Fatigue 2001 23 897 902
- Sugiura , R. , Yokobori , A. T. , and Tabuchi , M. , Yokobori , T. Comparison of creep crack growth rate in heat affected zone of welded joints for 9% Cr ferritic heat resistant steel based on C *, dδ / dt, K, Q * parameters Engineering Fracture Mechanics 2007 74 868 881
- Newman , J.C. Jr. , Raju , I.S. Analysis of surface cracks in finite plates under tension or bending loads NASA Technical Paper 1578 National Aeronautics and Space Administration December 1979
- Cheng , H. , Yang , F. , and Wei , Z. Potential Failure Modes and Accelerating Test Strategy of Burner SAE Technical Paper 2012-01-0523 2012 10.4271/2012-01-0523
- Nagode , M. and Hack , M. The Damage Operator Approach: Fatigue, Creep and Viscoplasticity Modeling in Thermo-Mechanical Fatigue SAE Int. J. Mater. Manuf. 4 1 632 637 2011 10.4271/2011-01-0485