The Oxidation Effect in the Titanium Alloy at High Temperature

The aim of this paper is to study of oxidation effects in creep of the Ti-6Al-4V alloy, in different atmospheres (air, nitrogen and argon). The samples were treated during 24 hours at 600°C in different atmospheres The samples treated during 24 hours at 600°C and the oxidation behavior in each atmosphere was observed. The oxidation was more aggressive in air atmosphere, forming TiO₂ film in the surface. The alloy was tested in creep at 600°C in argon, nitrogen and air atmospheres using 250 MPa. The behavior of creep curves shows that useful life is better in atmospheres not so oxidant.