Resistance Spot Weldability of Three Metal Stack Dual Phase 600 Hot-dipped Galvanized Steel
Technical Paper
2007-01-1363
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
Fuel economy and federal safety regulations are driving automotive companies to use Dual Phase and other Advanced High Strength Steels (AHSS) in vehicle body structures. Joining and assembly plays a crucial role in the selection of these steels. Specifications are available for the resistance spot welding (RSW) of lower strength sheet steels, covering many aspects of the welding process from the stabilization procedure to endurance testing. Currently, specifications in the automotive industry for RSW with AHSS are limited. It is well known that welding of a thickness ratio greater than 1:2 poses a challenge. To utilize thinner gauge AHSS panels on body-in-white, welding schedules to join the thin to thick sheet steel stack-up are needed. Most of the existing published work was conducted on uncoated sheets and welded to the same thickness. This project was initiated to understand the RSW of a three-metal stack-up using AHSS - Dual Phase 600 (DP600) steel with a hot dip galvanized coating. As the use of welded joints involving thin to thick AHSS sheets become more common for vehicle body structures, the possibility of an extreme case of sheet thickness differential involving 1.9 and 0.8 mm gauges, both galvanized, is more likely. This study, through a Design of Experiments (DOE), quantified the effects of factors that included welding equipment (AC vs. MFDC), electrode shape (dome, 45º truncated and ISO 30º truncated), hold time, pulsing and weld current on joint strength (lap-shear and coach peel) for a three-metal thickness stack-up (0.8/1.9/1.9 mm). During the study a modified electrode stabilization procedure was developed and the hold-time sensitivity behavior at optimum button size was investigated. The current range, lap-shear tensile load, coach peel load and electrode life values were compared for each electrode type. The study was successful in identifying that the dome shaped electrode stabilizes faster, produces more consistent welds, and consumes less current, primarily due to its higher current density capability. The amount of weld current needed by the truncated electrodes was influenced by the electrode face angle. The dome shaped electrode produced a higher current range than the truncated cone electrodes. The dome electrode always produced the largest current range with the AC power source; no effect of the MFDC power source on the current range was observed. The number of pulses, or cool time between pulses, did not influence the current range. No hold time sensitivity was seen during the testing at 5 and 90 cycles hold time. A minimum of 2000 lbf (∼907 kgf) lap-shear tensile and 200 lbf coach peel loads were obtained with the dome electrode. Although the truncated cone electrodes produced an average load similar to the dome electrode, the results were more scattered. The endurance testing showed that the 45º truncated cone electrode provided the highest number of welds (∼1500), with the dome electrodes producing ∼1000 welds. Increasing weld current gradually and monitoring the voltage/resistance across the electrode was most effective in stabilizing the resistance spot welding electrodes. Overall, the dome electrode performed better than the truncated cone electrodes in welding a 0.8-1.9-1.9 mm DP600 HDG weld stack-up. The dome electrode is suggested for resistance spot welding of stack-ups with high thickness ratios.
Recommended Content
Authors
Topic
Citation
Coon, T., Elliott, A., Joaquin, A., Koganti, R. et al., "Resistance Spot Weldability of Three Metal Stack Dual Phase 600 Hot-dipped Galvanized Steel," SAE Technical Paper 2007-01-1363, 2007, https://doi.org/10.4271/2007-01-1363.Also In
References
- AWS D8.9 2002 Recommended practices for test methods for evaluating the resistance spot welding behavior of automotive sheet steel materials American Welding Society Miami, Florida, USA.
- A/S P technical report, AZ-017-02 997 1.0C EG, Auto/Steel Partnership, 2000 Town center, Suite 1900 Southfield, Michigan, USA
- Harsha Lalam Sree Agashe Soumitra Spot welding of advanced high strength steels using AC and MFDC power sources Sheet Metal Welding Conference XI May 2004 Detroit, Michigan, USA
- Dickinson D.W. Welding in the automotive industry report SG 81-5 August 1981 American Iron and Steel Institute 1000 16th street, N.W., Washington, D.C., USA
- Holt E. F. Sink L.W. Effects of nose design on spot welding Welding Journal May 1952 400 406
- Oak Ridge National Laboratories, USA, Three way coupled model allows one to depict the effects of electrode curvature on the weld development, http://mjndeweb.ms.ornl.gov/PNGV/Process/Bernie/Curvature/CurvatureEffectP.html
- Kaiser J.G. Dunn G.J. Eagar T. W. The effect of electrical resistance on nugget formation during spot welding Welding Research Supplement June 1982 167s 174s
- Brown B.M. A comparison of AC and DC resistance welding of automotive steels Welding journal Jan 1987 18 23
- Matsuyama Kin-ichi Polarity effect in DC resistance spot welding coated steels Sheet metal welding conference X May 2002 Detroit, USA
- Dickinson D. W. et al. Characterization of spot welding behavior by dynamic electrical parameter monitoring Welding Research Supplement June 1980 170s 176s
- A/S P technical report “Resistance Welding Design of Experiments for Coated Steels” January 2001 Auto/Steel Partnership, 2000 Town center, Suite 1900 Southfield, Michigan, USA