Plasma Process to Harden the Surface of Aluminum and Alloys
Technical Paper
2003-01-2921
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
Aluminum and its alloys are valued in structural applications for their excellent strength to weight ratio and several other desirable properties. However, their tribological properties in sliding friction are poor due to the softness of the bulk combined with the fragility of the native oxide. A method to harden the surface of small aluminum components has been developed. The process consists in immersing the object to be treated in a pulsed low pressure plasma using oxygen as working gas, and applying to it a high negative voltage (typically 30 kV). This drives the oxygen ions of the plasma into the piece to a depth of tens of nanometers (∼10-6 inch). This results in the formation of a layer of extremely fine-grained oxide precipitates in an aluminum matrix. The thickness of the layer is of the order of 0.1 μm (4 × 10-6 inch) and the precipitate size much less. The optimum results are obtained with a layer composition of about 50% oxide and 50% metal. The hardness of the treated layer, as measured by nanoindentation, is increased several fold up to values of 3 - 5 GPa (400 - 700 kpsi), while retaining good elasticity and ductilily. Nanoscratch test results show reductions in the scratch depths and the friction coefficients by nearly the same factors.
Recommended Content
Authors
Topic
Citation
Bolduc, M., Popovici, D., and Terreault, B., "Plasma Process to Harden the Surface of Aluminum and Alloys," SAE Technical Paper 2003-01-2921, 2003, https://doi.org/10.4271/2003-01-2921.Also In
References
- Metals Handbook , 1 8th ASM Metals Park, OH 1961 917
- Brandes E.A. Smithells Metals Reference Book 6th Butterworths London 1983
- Bourcier R.S. Myers S.M. Polonis D.H. Nucl. Instr. and Meth. B 44 278 1990
- Popovici D. Bolduc M. Terreault B. Sarkissian A.H. Stansfield B.L. Paynter R.W. Bourgoin D. J. Vac. Sci Technol. A 17 1996 1999
- Bolduc M. Popovici D. Terreault B. Surf. Coat. Technol 138 125 2001
- Conrad J.R. Radtke J. L. Dodd R.A. Worzola F.J. J. Appl. Phys. 62 4591 1987
- Bolduc M. Terreault B. Appl. Phys. Lett. 82 895 2003
- Hart R.K. Proc. R. Soc. A 236 68 1956
- Oliver W. C. Pharr G. M. J. Mater. Res. 7 1564 1992
- Gerberich E. W. Yu W. Kramer D. Strojny A. Bahr D. Lilleoden E. Nelson J. J. Mater. Res. 13 421 1998
- Digital Instrument Inc. Support Note No. 225, Rev. F Santa Barbara, CA 1998
- Ruan J.-A. Bhushan B. J. Tribol 116 378 1994
- Bolduc M. Terreault B. Reguer A. Shaffer E. St-Jacques R.G. J. Mater. Res
- Jagielski J. Piatkowska A. Aubert P. Legrand-Buscema C. Le Paven C. Gawlik G. Piekoszewski J. Werner Z. Vacuum 70 147 2003
- Orowan E. Symposium on Internal Stresses in Metals and Alloys Institute of Metals, London 1948 451