Semi-Solid Casting of Aluminium - Scandium (Zr) Foundry Alloys
Technical Paper
2001-01-3170
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
The New Rheocasting (NRC) process was applied to cast test specimens of the alloy AlSi7Mg plus minor additions of Scandium and Zirconium. In this paper the process for manufacturing of complex shaped components in semi-solid state is introduced. The semi-solid slurry is made from conventional melts by controlled cooling. There is no on - cost on the material. For comparison reasons the classical AlSi7Mg (A356) alloy was cast in a step plate die, heat treated and tested. The same treatment was given to A356 + Sc alloys. Small variations of chemical composition were chosen for the investigation of the formation of intermetallic phases and their behaviour during heat treatment.
Microstructural aspects and mechanical properties will be presented. It can be shown that additions of Scandium have a positive influence on hardness and strength of manufactured samples. The alloys show good castability and a fine grain structure which could be caused by the refining effect of Scandium in combination with Strontium. The adaptation of the well known alloy A356 with minor amounts of Scandium lead to new perspectives about using transition metals in semi-solid manufactured products.
Recommended Content
Authors
Citation
Hoelzl, A., Kaufmann, H., and Konkevich, V., "Semi-Solid Casting of Aluminium - Scandium (Zr) Foundry Alloys," SAE Technical Paper 2001-01-3170, 2001, https://doi.org/10.4271/2001-01-3170.Also In
References
- Lenczowski, B. Rauh, R. Wieser Tempus, G. Fischer, G. Becker, J. Folkers, K. Braun Lütjering, G. Weldable AlMgSc alloys for transportation technology Aluminium-76 2000 200 203
- Filatov, Yu. A. Deformable Al - Mg - Sc Alloys and Possible Regions of Their Application Journal of Advanced Materials 1995 5 386 390
- Belov, N. A. Aluminium eutectic casting alloys containing Scandium Int. Conference: Scandium and prospects of its use Moscow 18-19 October 1994 20
- Kaufmann H. Wabusseg H. Uggowitzer P.J. Metallurgical and processing aspects of the NRC Semi - Solid Casting Technology Aluminium-76 2000 69 75
- Kaufmann, H. Nakamura, M. Wabusseg, H. Uggowitzer, P. New Rheocasting: a novel approach to semi - solid casting Diecasting World Nov. 2000 14 17
- Uggowitzer P.J. Gullo G-C. Wahlen A. Kaufmann H. Uggowitzer P.J. 95 107
- Wabusseg, H. Kaufmann, H. Uggowitzer, .J. Struktur und Eigenschaften von New-Rheocasting Bauteilen Giesserei 87 2000 3 39 43
- Bushuev, Yu. G. Silis, V. E. Shul´gina, E. V. Dobrozhinskaya Aluminium alloys with Scandium. Development, Investigation and Application in Space Industry Int. Conference: Scandium and prospects of its use Moscow 18-19 October 1994 4
- Kaufmann, H. Mundl, A. Uggowitzer, P.J. 2001 27 32