Observations of the Relative Performance of Magnesium and Aluminum Steering Wheel Skeletons with Identical Geometry
Technical Paper
2000-01-0784
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Event:
SAE 2000 World Congress
Language:
English
Abstract
Automotive steering wheels depend on a structural skeleton made of steel, aluminum, or magnesium to be the basis for the mechanical properties of the finished part. The mechanical properties of concern are the fatigue properties and the crash performance. The purpose of this study was to evaluate the crash and the fatigue performance of a steering wheel skeleton fabricated by high pressure die casting. Two materials were used to produce two groups of wheels with identical geometry. The production part was designed, optimized and fabricated with AM50A magnesium. The production magnesium component met all of the regulatory design and performance requirements. A small sample run was made in a proprietary aluminum - magnesium alloy. The fatigue and crash properties were evaluated empirically.
In fatigue testing, the aluminum skeletons displayed a significant improvement, with respect to the magnesium skeletons, in the number of cycles to failure at the loads tested. Droptower impact tests were used to simulate a crash environment. The crash performance was described by an Energy Absorption Factor (E.A.F) and the Coefficient of Restitution. The results indicated that the aluminum skeletons absorbed more energy than the magnesium skeletons. The aluminum skeletons performed well under severe impact loading, while some cracking and fracture was observed in the magnesium parts. Further testing was performed to compare the crash performance of the two skeletons after fatigue cycling. There was no evidence of decay in crash performance after fatigue in the test conditions used.
Recommended Content
Citation
Ames, W. and Altenhof, W., "Observations of the Relative Performance of Magnesium and Aluminum Steering Wheel Skeletons with Identical Geometry," SAE Technical Paper 2000-01-0784, 2000, https://doi.org/10.4271/2000-01-0784.Also In
References
- Hydro Magnesium “Magnesium Casting Alloys”
- Rodrigo, D. Murray, M. Mao, H. Brevick, J. Mobley, C. Chandrasekar, V. Esdaile, E. “Effects of Section Size and Microstructural Features on the Mechanical Properties of Die Cast AZ91D and AM60B Magnesium Alloy Test Bars” SAE Technical Paper, Paper No. 1999-01-0927 Society of Automotive Engineers Warrendale, PA 1999
- Dierks, M.W. Kuhn, C. Etling, J. “Enhanced Mechanical Properties of Die Cast AM Series Magnesium; Through Part Design, Die Design and Process Control” SAE Technical Paper, Paper No. 940410 Society of Automotive Engineers Warrendale, PA 1994
- “Aluminum Foundry Products” Metals Handbook 10th 2 Properties and Selection: Non-Ferrous Alloys and Special Purpose Materials ASM International Materials Park, OH 1990