Nondestructive Characterization of Pitting Corrosion Damage and Fatigue Life
Annotation ability available
Sector:
Language:
English
Abstract
Microradiographical and ultrasonic methods for the determination of pitting corrosion depth is discussed. Fatigue crack initiation and growth from artificial pits of different depths is studied experimentally. The experime-ntal results were analyzed using fracture mechanics models including those for small cracks. The model shows very good agreement with experiment in describ-ing the initiation and growth of a crack emanating from a pit and in predicting the dependence of the reduction of fatigue life on pit size. Using this analysis, a relation between the depth of the corrosion pit and the fatigue life is established, and thus the prediction of fatigue life of the sample with corrosion pit is related to the radio-graphic and ultrasonic measurements.
Recommended Content
Technical Paper | Prediction of Lubricant's Fatigue Life in the FZG Micropitting Test |
Technical Paper | Corrosion and Fretting Effects on Fatigue |
Technical Paper | Corrosion Prevention and Control Programs for Boeing Airplanes |
Authors
Citation
Rokhlin, S., Zoofan, B., Kim, J., and Dai, W., "Nondestructive Characterization of Pitting Corrosion Damage and Fatigue Life," SAE Technical Paper 983127, 1998, https://doi.org/10.4271/983127.Also In
References
- Schmidt, H. J. Brandecker, B. Corrosion Fatigue Data and Design from an Aircraft Manu-facturer's Point of View. Fatigue '96, Proceedings of The Sixth International Fatigue Congress Berlin, Germany 643 654 1996
- Du, M. L. Chinging, F. P. Kajwada, S. V. Clayton, C. R. Synergism Between Corrosion and Fatigue of Al 2024-T3 Alloy Structural Integrity in Aging Aircraft, AD- 47 ASME 19 128 1995
- Scheuring, J. N. Grandt, A. F. A Fracture Mechanics Based Approach for Quantifying Corro-sion Damage Structural Integrity in Aging Aircraft, AD-47 ASME A7-1 A7-7 1996
- Nakajima, M. Tokaji, K. A Mechanical Condition of Fatigue Crack Initiation from Corrosion Pits Fatigue '96, Proceedings of The Sixth International Fatigue Congress Berlin, Germany 697 702 1996
- Becker, K. Rukwied, A. Allen, D. Knosp, B. Saisse, H. Brondsted, P. Bridge,. M. Lyon, M. The Effect of Surface Degradation on Fatigue and Fracture Behaviour Materials and Design 14 3 175 182 1994
- Chen, G. S. Wan, K.-C. Gao, M. Wei, R. P. Flournoy, T. H. Transition from Pitting to Fatigue Crack Growth - Modeling of Corrosion Fatigue Crack Nucleation in a 2024-T3 Aluminum Alloy Material Science and Engineering A219 126 132 1996
- Philips, E. P. Neuman, J. C. Impact of Small Crack Effect on Design Life Calculations Experimental Mechanics 221 225 1989
- Domarkas, V. Khuri-Yakub, B. T. Kino, G. S. Length and Depth Resonances of Surface Cracks and Their Use for Crack Size Estimation Appl. Phys. Lett. 33 7 1978 557 559
- Ayter, S. Auld, B. A. On the Resonances of Surface Breaking Cracks DARPA/AFML Rev. Quant. NDE 1980
- Mendelsohn, D. A. Achenbach, J. D. Keer, L. M. Scattering of Elastic Waves by a Surface-Breaking Crack Wave Motion 2 1980 277 292
- Buck, O. Thompson, R. B. Rehbein, D. K. Using Acoustic Waves for the Characterization of Closed Fatigue Cracks Mechanics of Fatigue Crack Closure , ASTM STP 982 Newman, J. C. Jr. Elber, W. 1988 536 547
- Zoofan B. Rokhlin S. I. Microradiographic Detection of Corrosion Pitting Materials Evaluation 56 2 191 194 1998
- Allison, J. E. The Measurement of Crack Closure During Fatigue Crack Growth Fracture Mechanics : Eighteen Symposium , ASTM STP 945 Read, D. T. Reed, R. P. 1988 913 933
- Phillips, E. P. The Influence of Crack Closure on Fatigue Crack Growth Thresholds in 2024-T3 Aluminum Alloy Mechanics of Fatigue Crack Closure, ASTM STP 982 Newman, J. C. Jr. Elber W. 505 515 1988
- Raju, I. S. Newman, J. C., Jr. Stress-intensity Factors for Two Symmetric Corner Cracks Fracture Mechanics, ASTM STP 677 Smith C. W. 411 430 1979
- Green, A. E. Sneddon, I. N. The Distribution of Stress in the Neighborhood of a Flat Elliptical Crack in an Elastic Solid Proc. Cambridge Phil. Soc. 46 1950
- Tada, H. Paris, P. C. Irwin, G. R. The Stress Analysis of Crack Handbook Del Research Corporation Hellertown, PA. 2.2 1973
- Elber, W. Fatigue Crack Closure Under Cyclic Tension Engng Fracture Mech. 12 1 37 45 1970
- Newman J. C. Jr., An Improved Method of Collocation For the Stress Analysis of Cracked Plates With Various Shaped Boundaries NASA Technical Note, NASA TN D-6376 1971
- Rolfe, S. T. Barsom, J. M. Fracture and Fatigue Control in Structures Applications of Fracture Mechanics Prentice Hall NJ 42 1987
- Newman, J. C. Raju, I. S. An Empirical Stress-Intensity Factor Equation for the Surface Crack Engng Fracture Mech. 40 185 192 1981
- de Koning, A. U. A Simple Crack Closure Model for Prediction of Fatigue Crack Growth Rates under Variable-Amplitude Loading Fracture Mechanics, ASTM STP 743 Roberts R. 63 85 1981
- Ewalds, H. L. Wanhill, R. J. H. Fracture Mechanics Arnold Edward Maatschappij Delftse Uitgevers MD 173 1984