Silver Alloy, Brazing Filler Metal 40Ag - 30Cu - 30Zn 1245 to 1340 °F (674 to 727 °C) Solidus-Liquidus Range
- Aerospace Material Specification
- AMS4762B
- Revised
Scope
Rationale
Recommended Content
Aerospace Material Specification | Silver Alloy, Brazing Filler Metal 40Ag - 30Cu - 30Zn 1245 to 1340 °F (674 to 727 °C) Solidus-Liquidus Range |
Aerospace Material Specification | Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 30Au - 34Pd - 36Ni 2075 to 2130 °F (1135 to 1166 °C) Solidus-Liquidus Range |
Aerospace Material Specification | Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 70Au - 8.0Pd - 22Ni 1845 to 1915 °F (1007 to 1046 °C) Solidus-Liquidus Range |
Topic
Data Sets - Support Documents
Title | Description | Download |
---|---|---|
Unnamed Dataset 1 | ||
Table 1 | Composition | |
Table 2 | Standard diameter sizes | |
Table 3A | Diameter tolerances, inch/pound units | |
Table 3B | Diameter tolerances, SI units | |
Table 4 | Standard thicknesses | |
Table 5 | Particle size distribution |
Issuing Committee
AMS D Nonferrous Alloys Committee
The committee of Nonferrous Alloys, AMS Committee D, shall prepare, coordinate, and revise documents related to nonferrous metals technology, such as aluminum, magnesium, and copper, through the participation of metals suppliers, users, and interested government agencies. Committee activities shall provide a forum for the cooperative interchange of ideas and experience of the participants, resulting in the publication of specifications that embody sound, established aerospace industry practices and requirements to serve the suppliers and customers of aerospace materials.