Yarn, Organic Fiber (Para-Aramid), High Modulus OY 390 (2689)/23.9 Tensile Strength, 16.5 (114)/900 Tensile Modulus 1140 Denier (1270 d tex), 0.6% Finish
- Aerospace Material Specification
- AMS3901/3C
- Revised
Downloadable datasets available
Annotation ability available
Sector:
Issuing Committee:
Language:
English
Scope
This specification covers one type of organic fiber in the form of yarn. The product shall be formed as a multiplicity of filaments drawn together and gathered into an approximately parallel arrangement.
Topic
Data Sets - Support Documents
| Title | Description | Download |
|---|---|---|
| TABLE 1 | Properties |
Issuing Committee
AMS P Polymeric Materials Committee
Welcome to the AMS-P Polymeric & Composites Materials Committee discussion forum.
The AMS-P Polymeric Materials Committee writes and revises Aerospace Material Specifications (AMS), Metric Aerospace Materials Specifications (MAM), Aerospace Recommended Practices (ARP), and Aerospace Information Reports (AIR) for composite material technology as assigned to the committee. No copyrighted material may be posted in this forum. SAE is not liable for opinions expressed or information posted to this forum. All information posted becomes the property of SAE.Reference
| Number | Title |
|---|---|
| ANSI/ASQZ1.4 | This document is not part of the subscrption. |
| ASTMD1907 | This document is not part of the subscrption. |
| ASTMD2343 | This document is not part of the subscrption. |
| ASTMD885 | This document is not part of the subscrption. |
* Redlines comparisons are available for those standards
listed in the Revision History that contain a radio button. A
redline comparison of the current version against a revision is
accomplished by selecting the radio button next to the standard and
then selecting 'compare'. At this time, Redline versions only exist
for some AMS standards. SAE will continue to add redline versioning
with ongoing updates to SAE MOBILUS.