Effects of Temperature and Crack Tip Opening Rate on Fracture Behavior of CNBR Modified Epoxy Adhesives Under Mode I Loading
Annotation ability available
Sector:
Language:
English
Abstract
The effects of temperature, crack tip opening rate and rubber content on static fracture characteristics of CNBR (Cross-linked acryloNitrile Butadiene Rubber) modified epoxy adhesives were investigated under mode I loading. Loading-unloading tests were statically performed by using DCB (Double Cantilever Beam) specimens.
The fracture toughness increased with increasing the rubber content. The fracture toughness of CNBR modified and unmodified epoxy adhesives was much influenced by temperature and crack tip opening rate. The surface topology of fractured surface was changed by temperature and type of adhesive.
Citation
Kimura, K., Naito, K., and Fujii, T., "Effects of Temperature and Crack Tip Opening Rate on Fracture Behavior of CNBR Modified Epoxy Adhesives Under Mode I Loading," SAE Technical Paper 970661, 1997, https://doi.org/10.4271/970661.Also In
References
- Kinloch A.J. Structural Adhesives Elsevier Applied Science Publishers 1986 127 200
- Yee A.F. Pearson R.A. “Fractgraphy and Failure Mechanisms of Rubber Modified Epoxide Resins” Fractography and Failure Mechanisms of Polymers and Composites Ann Arbor Department of Materials Science and Engineering, University of Michigan Michigan, USA 292 350
- Ueno T. “Toughening of Epoxy Resins by Modification with Cross linked Rubber,” 31 11 1995 471 478
- Mall S. Ramamurthy G. “Effect of Bond Thickness on Fracture and Fatigue Strength of Adhesive Bonded Composite Joints,” International journal of adhesion and adhesives 9 1 1989 33 37
- Kobayashi H. Hakairikigaku Kyouritu Syuppan Inc. 1993 46
- Okamura H. Senkei Hakai Rikigaku Nyuumon Baifuukann 1976 154
- Smiley A.J. Pipes R.B. “Rate Effects on Mode I Interlaminar Fracture Toughness in Composite Materials,” Journal of Composite Materials 21 July 1986 670 687
- Tsuchida Masahiro NAITO Kimiyoshi FUJII Toru “Effects of CNBR Modification on Mode I Fracture of Epoxy Adhesives for Automotive Application” SAE Technical Paper Series 1995