Fatigue Fracture Characteristics of Toughened Epoxy Adhesive Under Mode I Loading - Effects of Glass Beads and CNBR Rubber Modification
Annotation ability available
Sector:
Language:
English
Abstract
The effects of inclusion of glass beads and rubber modification on the fatigue fracture characteristics of an epoxy adhesive were investigated. Hybrid effects were also investigated when not only the epoxy adhesive was rubber modified but also when glass beads were mixed simultaneously.
Fatigue crack growth resistance was greatly increased due to glass beads, CTBN and CNBR modifications at the second stage of crack growth (da/dN=10-4-10-3 mm/cycle). However, the energy release rate at threshold for both CNBR and CTBN modified adhesives were lower than that for the unmodified adhesive. No significant hybrid effects were distinguishable.
Citation
Hayashi, S., Naito, K., and Fujii, T., "Fatigue Fracture Characteristics of Toughened Epoxy Adhesive Under Mode I Loading - Effects of Glass Beads and CNBR Rubber Modification," SAE Technical Paper 960576, 1996, https://doi.org/10.4271/960576.Also In
References
- Hunston D. L. Bascom W. D. “Failure behavior of rubber-toughened epoxies in bulk, adhesive, and composite geometries,” American Chemical Society 1983 83 99
- Spanoudakis J. Young R. J. “Crack propagation in a glass particle-filled epoxy resin,” Journal of Material Science 19 1984 473 486
- Nejigaki K. “Properties of toughened epoxy resin,” PLASTICS 43 11 1992 139 145
- Tsuchida M. Naito K. Fujii T. “Effectcs of CNBR modificatin on Mode I Fracture of Epoxy Adhesives for Automotive Application,” SAE TECHNICAL PAPER SERIES, 950130 1994
- Narisawa I. Kobunshi Kyodogaku Omusha 1982 323
- Mall S. Ramamurthy G. “Effect of bond thickness on fracture and fatigue strength of adhesively bonded composite joints,” Int. J. Adhesion and Adhesives 9 1 1989 33 37
- Naito K. Fujii T. “Fractals for fractured surfaces of adhesives under static and fatigue loadings,” Int. J. Adhesion and Adhesives 15 3 1995 123 130
- Xu X.X. Crocrombe A. D. Smith P. A. “Fatigue behavior of joints bonded with either filled, or filled and toughened, adhesive,” Fatigue 16 1994 469 477
- Vasudevan A. K. Sadananda K. Louat N. “Reconsideration of Fatigue Crack Closure,” Scripta METALLURGICA et MATERIALIA 27 1992 1673 1678