“Fatigue Behavior of Sheet Steels for Automotive Industry”
Annotation ability available
Sector:
Event:
SAE Brasil
Language:
English
Abstract
Carbon and rephosphorized pre-strained sheet steels for cold drawing forming operations were studied and the tensile, high cycle fatigue and fatigue crack propagation properties were determined. The fatigue limit was found to be higher for 20% than for 1% pre-strained condition. Threshold stress intensity factors (▵Ků) of 5.29 MPa. m1/2 for rephosphorized steel and 7.07 MPa. m1/2 for carbon steel. Critical crack lenghts were calculated by ▵Ků and fatigue limit data using the Lukas-Klesnil short-crack criterion. Through fractographic analysis it was possible to determine the general behavior of tested materials near threshold.
Recommended Content
Technical Paper | Fatigue Properties of High Pressure Die-Cast Magnesium AM60B Alloy |
Technical Paper | Prestrain Effect on Fatigue of DP600 Sheet Steel |
Technical Paper | Fatigue Properties of Sheet Steel Before and After Galvanizing |
Authors
- Luiz Vicente Vareda - Departamento de Materiais - EESC - USP, Departamento de Engenharia Materiais - UFSCar
- Dirceu Spinelli - Departamento de Materiais - EESC - USP, Departamento de Engenharia Materiais - UFSCar
- Isa Müller-Spinelli - Departamento de Materiais - EESC - USP, Departamento de Engenharia Materiais - UFSCar
Topic
Citation
Vareda, L., Spinelli, D., and Müller-Spinelli, I., "“Fatigue Behavior of Sheet Steels for Automotive Industry”," SAE Technical Paper 921439, 1992, https://doi.org/10.4271/921439.Also In
References
- BORDIGNON, P. J. P. HULKA, K. JONES, B. L. High strength low-alloy steels for automotive applications Niobium Technical Report SãoPaulo 1 45 Dez. 1984
- LUKAS, P. KLESNIL, M. Fatigue limit of notched bodies Mat.Scien.and Eng. 34 61 6 1978
- LUKAS, P. et alli Non-damaging notches in fatigue Fatigue & Fract.Eng.Mat.and Struct. 9 3 195 204 1986
- ASTM-Standard test methods for determining average grain size (ASTM E 112) 284 309 1988
- ASTM-Standard methods and definitions for mechanical testing of steel products. (ASTM A 370) 188 243 1981
- ASTM-Standard test method for plastic strain ratio for sheet metal (ASTM E 517) 657 64 1982
- ASTM-Standard test method for tensile strain-hardening exponents (n-values) of metallic sheet materials (ASTM E 646) 762 71 1982
- ASTM-Standard recommended practice for constant amplitude axial fatigue test of metallic materials. (ASTM E 466) 635 75 1976
- ASTM-Standard test method for measurement of fatigue crack growth rates (ASTM E 647) 636 54 1988
- VAREDA, L.V. SPINELLI, D. MULLER-SPINELLI, I. 4 567 87 1991
- SPERLE, J. O. Proposal for additions to fatigue design code. T 10303-4 ASEA Int. Rep.KYBA 68 14 1968
- SPERLE, J.O. Fatigue strength of high strenght dual phase steel sheet Int. J. of Fatigue 7 2 79 86 1985