Effect of Coating Structure on Powdering Resistance of Galvannealed Steel Sheet
Annotation ability available
Sector:
Language:
English
Abstract
Galvannealed steel sheets containing 10wt%Fe in coated layer were prepared in various galvannealing temperature and cooling rate. Powdering resistances were evaluated by a draw bead test. X-ray diffraction examination revealed an attribution of the coating structure to powdering resistance.
Higher galvannealing temperature(500∼550°C) deteriorates powdering resistance, but slower cooling from higher temperature improves it. At low galvannealing temperature(440°C), powdering resistance is rather good independent of cooling rate. Г1-phase(Fe5Zn21) is formed along the interface between coating and steel when samples are galvannealed at lower temperature(≦500°C) or cooled at slower cooling rate from higher galvannealing temperature. The results suggest that the increase of Г1 ratio [Г1/(Г+Г1)] in the coating is inclined to improve powdering resistance.
Recommended Content
Authors
Citation
Sakurai, M., Zhang, L., Tajiri, Y., and Kondo, T., "Effect of Coating Structure on Powdering Resistance of Galvannealed Steel Sheet," SAE Technical Paper 920174, 1992, https://doi.org/10.4271/920174.Also In
References
- Inagaki J. Nakamura S. Yoshida M. Nishimoto A. SAE paper 890349 1989
- Nakamori T. Shibuya A. Proc. on World Materials Cong. of Corrosion-Resistant Automotive Sheet Steels, Int. ASM 139 1988
- Yasuda A. Koumura H. Yamato K. Onizawa K. Ota H. Proc. on World Materials Cong. of Corrosion-Resistant Automotive Sheet
- Lucas P.L. Quantin D. Brun C.G. Proc. of the Int. Conf. on Zinc and Zinc alloy coated Steel Sheet(GALVATECH) 138 1989
- Urai M. Terada M. Yamaguchi M. Nomura S. Proc. of the Int. Conf. on Zinc and Zinc Alloy coated Steel Sheet(GALVATECH) 478 1989
- Tokunaga Y. Yamada M. Hada T. (Journal of the Iron and Steel Institute of Japan) 70 997 1984
- Nakayana M. Numakura Y. Kanamaru T. CAMP-ISIJ 3 649 1990
- Tajiri Y. Shimada S. Sakurai M. Adaniya T. SAE paper 900508 1990
- Gellings P.J. de Bree E.W. Gierman G. Metallkd Z. 70 312 1979
- Gellings P.J. de Bree E.W. Gierman G. Metallkd Z. 70 312 1979
- Gellings P.J. Gierman G. Koster D. Kuit J. Metallkd Z. 71 70 1980
- Nakamori T. Sakane T. Toki T. Current Advances in Materials and Processes 2 5 1702 1989