Evaluation of Residual Stresses, Grinding Burns and Heat Treat Defects Through Chrome Plating
Annotation ability available
Sector:
Language:
English
Abstract
Determining residual stresses and detecting material defects through coatings is difficult with conventional testing techniques. X-ray diffraction can be used for residual stress determination on bare surfaces of a variety of materials, but fails to give any indication of stress in the underlaying metal through coatings. Nital etching cannot be used to detect grinding burns unless coating is removed. To overcome these difficulties, magnetic Barkhausen noise technique was used to study the feasibility of determining stresses and detecting grinding burns and heat treat defects through chrome plating.
Test results suggest that the sensitivity of Barkhausen noise technique to defects and residual stresses through chrome is excellent up to plating thicknesses of 0.012 in. (0.3 mm). This technique can replace the presently used procedures to determine stress and to detect material defects through coatings.
Recommended Content
Aerospace Material Specification | Plating, Brush, Zinc-Nickel Low Hydrogen Embrittlement |
Aerospace Material Specification | Heat Treatment Austenitic Corrosion-Resistant Steel Parts |
Technical Paper | Die Materials and Treatments with Electrogalvaniied Steels |
Authors
Citation
Tiitto, K. and Fix, R., "Evaluation of Residual Stresses, Grinding Burns and Heat Treat Defects Through Chrome Plating," SAE Technical Paper 880877, 1988, https://doi.org/10.4271/880877.Also In
References
- DUNN F W Magnetic Particle Inspection Fundamentals Materials Evaluation Dec. 1977 42 47
- Temper Etch Inspection 1979
- HILLEY M E LARSON J A JATCZAK C F RICKLEFS R E Residual Stress Measurement by X-ray Diffraction SAE J784a 1971
- Determining Residual Stresses by the Hole-Drilling Strain-Gage Method ASTM Standard E837-85, Annual Book of ASTM Standards 03.01 1987
- BARKHAUSEN H Zwei mit Hilfe der Neuen Verstaerker Entdeckte Erscheinungen 20 1919 401 403
- ZSCHIESCHE K Uber Magneto-elastische Effekte 23 1922 201 214
- PASHLEY R L Barkhausen Effect - An Indication of Stress Materials Evaluation 28 1970 157 161
- TIITTO S On the Influence of Microstructure Magnetization Transitions in Steel Acta Polytechnica Scandinavica Helsinki 1977
- TIITTO K Use of Barkhausen Effect in Testing for Residual Stresses and Material Defects Proceedings of ASM's Conference on Residual Stress - In Design, Process and Materials Selection Young W. 1987 27 36