Mechanism of Corrosion and Delamination of Painted Phosphated Steel During Accelerated Corrosion Testing
Annotation ability available
Sector:
Language:
English
Abstract
A THEORETICAL MODEL for the delamination of organic coatings from zinc-phosphated steel surfaces will be presented. It will be shown that under ambient conditions and in neutral NaCl media delamination occurs as a result of the formation of a surface-tension gradiant during oxygen depolarization and, subsequently, the disruption of adhesion at the coating-phosphate interface. Dissolution of the phosphate coating occurs only after adhesion is lost. An accelerated cathodic delamination test showing good correlation with the long-term GM-scab test will also be introduced.
Recommended Content
Aerospace Material Specification | Columbium (Niobium) Alloy Sheet, Strip, and Plate, 10Hf - 1.0Ti |
Aerospace Material Specification | Titanium Alloy Bars, Forgings, and Rings 5Al - 2.5Sn, Extra Low Interstitial Annealed |
Aerospace Material Specification | Columbium (Niobium) Alloy Foil, Sheet, Strip, and Plate 10W - 2.5Zr Recrystallized |
Authors
Citation
Knaster, M. and Parks, J., "Mechanism of Corrosion and Delamination of Painted Phosphated Steel During Accelerated Corrosion Testing," SAE Technical Paper 860110, 1986, https://doi.org/10.4271/860110.Also In
References
- Ritter J. J. Kruger J. Corrosion Control by Organic Coatings Leidheiser H., Jr. NACE Houston, Tx. 1981
- Maeda Shigeyoski Journal of Coating Technology 55 707 Dec. 1983
- Zurila R. W. Hospadaruk V. SAE Annual Meeting, Paper No. 780187 1978
- Davis J. W. SAE Annual Meeting, Paper No. 820336 1982
- Slane J. A. Clough S. P. Nappier J. R. Mettallurg Trans. 9A 1839 1978
- Knaster M. Davis J. W. Electrocoat Annual Meeting Technical Paper Cincinnati, Oh. 1982
- Davis J. W. Knaster M. SAE Annual Meeting, Paper No. 830495 1983
- Leroy V. Servails J. P. NACE Annual Meeting L.A. 1985
- International Publication under Patent Cooperation Treaty, No. WO 84/00386 1984
- Takahashi M. Matsudo K. et al. SAE Annual Meeting, Paper No. 800145 1980
- Mansfeld F. Kendig M. W. Tsai S. Corrosion 38 570 1982
- Leidheiser, H. Jr. Corrosion Source Book ASM and NACE 215 1984
- Leidheiser, H. Jr. Kendig M. W. Corrosion 32 69 1976
- Parks J. Lehigh University 1985
- Handbook of Chemistry and Physics 38th 1956-57
- Wagner C. Traud W. J. Electrochem. 44 391 1938
- Knaster M. Journal of Metal Protection (Russ.) 3 3 167 1967
- Knaster M. J. Electrochem. Soc. 124 3 94c 1977
- Knaster M. Steinbrecher L. Proceedings of the ACS Division of Polymeric Materials 53 703 1985
- Frumkin A. N. Bagotzki V. S. et al Study of Electrode Kinetics, Edition of Moscow University 26 1952