Formability of Galvanized Steels - Revisited
Annotation ability available
Sector:
Language:
English
Abstract
A series of sheet steels with corrosion-resistant coatings was tested, by punch stretching and in tension, in both the as-received condition and after the zinc was removed chemically. The results obtained indicate that the reduced formability of galvanized steels cannot be attributed to an increase in punch-sheet friction. The punch stretching data were well explained by a model which results in the generation of local tensile stresses leading to premature failure in regions of negative curvature which contact the punch. This model is compatible with the observation that the limiting dome height in punch stretching decreases with increasing intermetallic layer thickness. The model is also compatible with the observation that no such correlation is observed between alloy layer thickness and tensile ductility.
Recommended Content
Technical Paper | Prediction of Draw Bead Coefficient of Friction Using Surface Temperature |
Aerospace Material Specification | Steel, Welding Wire 0.80Cr - 1.8Ni - 0.25Mo (0.35 - 0.40C) (SAE 4340 Mod) Vacuum Melted, Environment-Controlled Packaging |
Aerospace Material Specification | Steel, Corrosion and Heat-Resistant, Sheet, Strip, and Plate 17Cr - 13Ni - 2.5Mo (316L) Solution Heat Treated |
Citation
Stevenson, R., "Formability of Galvanized Steels - Revisited," SAE Technical Paper 850276, 1985, https://doi.org/10.4271/850276.Also In
References
- Knauschner A. Menzel H.-U. Neue Hutte 23 28 1978
- Aoki I. Horita T. Herai T. proceedings of ‘Technological Impact of Surfaces’ ASM/ADDRG Conference 14/15 April 1981 Dearborn, Michigan
- Meuleman D. J. Denner S. G. Cheng F. S. SAE Paper 840370 Detroit, Michigan 1984
- Hecker S. S. Sheet Metal Industries 52 671 1975
- Ghosh A. K. Metals Engineering Quarterly 15 53 August 1975
- Ayres R. A. Brazier W. G. Sajewski V. F. J. Applied Metalworking 1 41 1975
- Stevenson R. Journal of Applied Metalworking 3 272 1984
- Rowland D. H. Trans. ASM 40 983 1948
- Ghosh A. K. Met. Trans. A. 7A 523 1976
- Mackowiak J. Short N. R. Int. Metals. Reviews, Review 237 1 1 1979
- Borzillo A. R. Hahn W. C. Jr. Trans. ASM 62 729 1969
- Bucher J. H. Hamburg E. G. ‘Formable HSLA and Dual-Phase Steels’ Davenport A. T. 1979 AIME 144
- Nishmoto A. Hosoya Y. Wakaoka A. presented at a Symposium on Fundamentals of Dual Phase Steels held in conjunction with the 110th Annual Meeting of AIME Chicago, Ill. Feb. 1981
- Sih G. C. Paris P. C. Erdogan Fe. J. Appl. Mech. 29 SAI Trans. E 84 307 1962