Cosmetic Corrosion Mechanism of Zinc and Zinc Alloy Coated Steel Sheet for Automobiles
Annotation ability available
Sector:
Language:
English
Abstract
Water penetration into the paint film of car bodies causes cosmetic corrosion. The circumstances experienced by driven cars can be classified into three groups, corresponding to high, medium and low water migration, respectively. In the first group a lot of water enters into the paint/substrate interface and lifts up the film. The stability of the phosphate layer influences the adhesiveness. In the second group salt water brings about alkaline blister formation. The corrosion resistance of the substrate against alkali in cathodically polarized state determines the paint adhesion. The third group corresponds to the scab corrosion, which can be suppressed well by zinc coating layer.
Recommended Content
Authors
- Yasuhiko Miyoshi - Nippon Steel Corp., Research and Development Laboratories-II, Surface Treatment Research Laboratory Sagamihara, Japan
- Minoru Kitayama - Nippon Steel Corp., Research and Development Laboratories-II, Surface Treatment Research Laboratory Sagamihara, Japan
- Kazumi Nishimura - Nippon Steel Corp., Research and Development Laboratories-II, Surface Treatment Research Laboratory Sagamihara, Japan
- Shigeru Naito - Nippon Steel Corp., Research and Development Laboratories-II, Surface Treatment Research Laboratory Sagamihara, Japan
Citation
Miyoshi, Y., Kitayama, M., Nishimura, K., and Naito, S., "Cosmetic Corrosion Mechanism of Zinc and Zinc Alloy Coated Steel Sheet for Automobiles," SAE Technical Paper 850007, 1985, https://doi.org/10.4271/850007.Also In
References
- Miyoshi Y. Kitayama H. Ito Y. Koyahara H. “A Study of Corrosion Test Methods for Automotive Steel Sheet.” SAE Paper 840210 February 27 March 2 1984
- Kent G. D. Hacias K. J. Fotinos N. A. “Laboratory Evaluation of Automotive Conversion Coatings.” SAE Paper 831812 December 5-7 1983
- Standish J. V. Whelan G. W. Roberts T. R. “The Corrosion Behavior of Galvanized and Cold Rolled Steels.” SAE Paper 831810 December 5-7 1083
- McArthur H. “Accelerated Corrosion Tests in the Motor Industry.” J. Oil Col. Chem. Assoc. 65 306 1982
- Kitayama M. et al Tetsu-to-Hagane
- Saito T. Odashima H. Hirano Y. Kitayama M. “Wet Adhesion of Zn-Ni Alloy Coated Steel Sheet.” Tetsu-to-Hagane 70 5 S461 1984
- Ruggeri R. T. Beck T. R. “An Analysis of Mass Transfer in Filiform Corrosion.” Corrosion 39 11 452 1983
- Westberg J. Borjesson L. “Influence of Sheet Metal Surface Conditions on the Corrosion Properties of Automotive Paint Systems.” Paper 278 International Corrosion Forum Chicago March 1980
- Miyoshi Y. Yoshida K. Azami T. Kanamaru T. Kado S. “On the Corrosion Behavior of Painted Galvannealed Steel Sheet.” Tetsu-to-Hagane 66 7 858 1980