Properties of Formable High Strength Sheet Steels for Automotive Use
Technical Paper
830883
Annotation ability available
Sector:
Language:
English
Abstract
Metallurgical factors affecting the press formability of the newly developed high strength sheet steels have been discussed. Dual phase steels, CHLY(cold-rolled sheet steel) and HTP-D(as-hot-rolled sheet steel), produced by control of cooling conditions after intercritical annealing or hot-rolling exhibit very low yield to tensile strength ratio and high n-value. Rephosphorized extra-low carbon steel, CHRX, produced by continuous annealing with rapid cooling is characterized by its extremely high r-value and low yield strength. CHLY, HTP-D and CHRX have large bake hardenability. Precipitation hardened steel, HTP-F(hot-rolled sheel steel), produced by adjusting carbon equivalent and sulfur content is suitable for manufacturing wheel rims owing to its good formability after flash butt welding.
Recommended Content
Aerospace Material Specification | Steel, Corrosion Resistant, Bars, Wire, Forgings, Mechanical Tubing and Rings 16Cr - 4.0Ni - 0.30Cb (Nb) - 4.0Cu Solution and Precipitation Heat Treated (H1025) |
Aerospace Material Specification | Steel, Sheet, Strip, and Plate 0.95Cr - 0.20Mo (0.28 - 0.33C) (SAE 4130) Normalized or Otherwise Heat Treated |
Aerospace Material Specification | Steel Bars 0.95Cr - 0.20Mo (0.28 to 0.33C) (SAE 4130) Hardened and Tempered, 125 Ksi (862 MPa) Tensile Strength |
Authors
- Susumu Satoh - Kawasaki Steel Corporation, Japan
- Akio Tosaka - Kawasaki Steel Corporation, Japan
- Toshiyuki Kato - Kawasaki Steel Corporation, Japan
- Masatoshi Shinozaki - Kawasaki Steel Corporation, Japan
- Takashi Obara - Kawasaki Steel Corporation, Japan
- Minoru Nishida - Kawasaki Steel Corporation, Japan
Citation
Satoh, S., Tosaka, A., Kato, T., Shinozaki, M. et al., "Properties of Formable High Strength Sheet Steels for Automotive Use," SAE Technical Paper 830883, 1983.Also In
References
- Tanaka T. Nishida M. Hashiguchi K. Kato T. “Structure and Properties of Dual-Phase Steels” Proceedings of AIME Anual Meeting in New Orleans 1979 221
- Kato T. Hashiguchi K. Takahashi I. Irie T. Ohashi N. “Fundamentals of Dual-Phase Steels” Proceedings of AIME 1981 199
- Mano J. Nishida M. Tanaka T. Kato T. Aoyagi N. Yamada N. Tetsu-to-Hagané 68 1982 9 171
- Ohashi N. Irie T. Satoh S. Hashimoto O. Takahashi I. SAE paper No. 810027 1981
- Hashimoto O. Satoh S. Irie T. Ohashi N. “Advances in the physical metallurgy and applications of steels” Proceeding of The Metals Society in Liverpool 1981 95
- Irie T. Satoh S. Yasuda A. Ohashi N. “Metallurgy of Continuous-Annealed Sheet Steel” Proceedings of the TMS-AIME symposium in Dallas 1982 155
- Shinozaki M. Matsumoto Y. Kato T. Nishida M. SAE paper No. 830279 1983
- Fukuda N. Shimizu M. J. Japan Soc. Technol. Plasticity 13 1972 841
- Hook R.E. Elias J.A. Met. Trans. 3 1972 2171
- Satoh S. Irie T. Hashimoto O. Tetsu-to-Haganè 69 1983 2 283
- Irie T. Satoh S. Hashiguchi K. Takahashi I. Hashimoto O. Trans. ISIJ 21 1981 793