Copper Bearing High Strength Cold Rolled Steel Sheets with Superior Drawability
Annotation ability available
Sector:
Language:
English
Abstract
Copper and phosphorus bearing high strength cold rolled steel sheets with superior drawability have been developed. The copper and phosphorus contents of these steels are 0.6% and 0.08% respectively. The tensile strengths of the steels are 500–550 MPa and the r values are as high as 1.5–1.7. The excellent r values of these steels are obtained by the precipitation treatment of 650° C × 10 hrs before cold rolling. This high r value is considered to be caused by the copper precipitates occured during this heat treatment. Both silicon and manganese strengthened copper bearing steels are investigated. High-silicon steels have better elongation than high-manganese steels. As to the r value, however, the latter are superior. In order to obtain excellent r value, high reduction in cold rolling and slow heating in annealing are required in addition to the precipitation treatment before cold rolling. The results of the trial production at Kobe Steel's Kakogawa Works showed good agreement with those of labolatory study.
Authors
Citation
Kameno, K., Nomura, S., and Kokubo, I., "Copper Bearing High Strength Cold Rolled Steel Sheets with Superior Drawability," SAE Technical Paper 820022, 1982, https://doi.org/10.4271/820022.Also In
References
- Ohashi N. Irie T. Satoh S. Hashimoto O. Takahashi I. SAE paper No. 810027 February 1981
- Jurkowski J.J. Gonzales M. SAE paper No. 790210 February 1979
- Takechi H. Takahashi N. Abe M. Akisue O. Koyama K. SAE paper No. 810028 February 1981
- Toda K. Gondoh H. Takechi H. Masui H. Metallurgical Transactions A 7A November 1976 1629 1636
- Hayami S. Furukawa T. Microalloying 75 78 87
- Satoh S. Irie T. Hashimoto S. Tetsu-to-Hagane 66 11 1980 S1123
- Teshima S. Shimizu M. Mechanical Working of Steel 2 1965 279 320 Gordon & Breach Scientific Pub.
- Hutchinson W. B. Duggan B. J. Metal Science August 1978 372 380
- Leslie W. C. Trans AIME 221 August 1961 752 758
- Shimizu M. Takahashi N. Suemune K. Tetsu-to-Hagane 58 4 1972 S267
- Wacquez P. Daele R. V. Sheet Metal Industries January 1967 21 30
- Ricket R. L. Leslie W. C. Transactions of the ASM 51 1959 310 334
- Abe H. Suzuki T. Miyasaka N. Togawa F. Tetsu-to-Hagane 59 11 1973 S649
- Ludwigson D.C. Schwerer F. C. Metallurgical Transactions 2 1971 3500 3501