Observations on Galvanic Corrosion Induced Paint Adhesion Loss
Annotation ability available
Sector:
Language:
English
Abstract
The locus of failure occurring with corrosion induced paint adhesion loss on the steel surface of one side galvanized sheet has been investigated using the scanning electron microscope. Controlled laboratory experiments to simulate alkaline attack of phosphate crystals in the conversion coating and bulk alkyd primer saponification have been used to provide a basis for interpreting the features observed on salt spray test panels, and on the back side of paint stripped after adhesion loss. The controlling failure mechanism is shown to be attack along primer-steel interfaces.
Recommended Content
Technical Paper | Perforation Resistance of Precoated Steels in an Accelerated Automotive Test |
Technical Paper | Solar Heat Reflecting Coatings |
Technical Paper | Waterborne Automotive OEM Primer Surfacer Makes a Splash in North America |
Authors
Citation
Roberts, T., Kolts, J., and Steele, J., "Observations on Galvanic Corrosion Induced Paint Adhesion Loss," SAE Technical Paper 800443, 1980, https://doi.org/10.4271/800443.Also In
References
- Hammond, J. S. Holubka, J. W. Dickie, R. A. “Surface Analysis of Interfacial Chemistry in Corrosion-Induced Paint Adhesion Loss” J. of Coatings Technology 51 45 1979
- Wiggle, R. R. Smith, A. G. Petrocelli, J. V. “Paint Adhesion Failure Mechanisms on Steel in Corrosive Environments” J. of Paint Technology 40 174 1968
- Wojtkowiak J. J. Bender, H. S. “Interrelationship between Steel Surfaces, Phosphatability, and Corrosion Resistance” J. of Coatings Technology 50 86 1978
- Hospadaruk, V. Huff, J. Zurilla, R. W. Greenwood, H. T. “Paint Failure, Steel Surface Quality and Accelerated Corrosion Testing” paper 780186 presented at SAE National Meeting, Detroit March 1978
- Cheever, G. D. “GMR Ferrotest” J. of Paint Technology 40 259 1969
- Zurilla R. W. Hospadaruk, V. “Quantitative Test for Zinc Phosphate Coating Quality” paper 780187 presented at SAE National Meeting, Detroit March 1978
- Evans U. R. Taylor, C. A. “Metal-Pigmented Paints for the Protection of Steel” Trans. Institute Metal Finishing 39 188 1962
- Tudor, W. E. “A Primer-Automotive Finishing and Corrosion Protection” paper 780914 presented at SAE Conference for Automotive Corrosion Prevention, Detroit,- November 1978
- Noller C. R. “Chemistry of Organic Compounds” W. B. Saunders Co. Philadelphia 170 1957
- Cheever G. D. Wojtkowiak, J. J. “Instrumental Studies of the Surface and Internal Composition of Paint Films” J. of Paint Technology 42 409 1970
- Neuhaus A Gebhardt M. “Interface Conversion for Polymer Coatings” Weiss P. Cheever G. D. American Elsevier New York 1968 91 119