Erosion Mechanisms of Automotive Spark Plug Electrodes
Annotation ability available
Sector:
Language:
English
Abstract
Scanning electron microscopy and microchemical analyses were conducted to determine the electrode erosion mechanisms of two different spark plugs, platinum-tip and nickel-alloy plugs, tested under various environments. The electrodes were eroded differently depending on the electrode materials and the operating environments. In bench test performed in a dry air pressure chamber, ejection of small molten particles from center electrodes and vaporization loss of side electrodes were the predominant erosion processes. In vehicle tests, the erosion mechanisms varied with the additives in the fuels used. Oxidation of base metal and electrode corrosion by fuel residues were the common erosion processes observed.
Recommended Content
| Technical Paper | Results of Multidimensional Tribodiagnostic Measurements |
| Technical Paper | Induction Period for Ignition of Fuel Sprays at High Temperatures and Pressures |
Authors
Citation
Young, C. and Grimes, D., "Erosion Mechanisms of Automotive Spark Plug Electrodes," SAE Technical Paper 780330, 1978, https://doi.org/10.4271/780330.Also In
References
- Goering W. A. “Spark Plug Electrode Materials and Erosion Mechanisms,” Technical Report No. AR-68-15 Ford Motor Company November 1968
- Asik J. R. “Erosion Mechanism for PROCO Spark Plugs,” Technical Report No. SR-75-8 Ford Motor Company January 1975
- Hoffman J. F. Champion Ignition Conference 1971 188 92
- Gray E. W. Pharney J. R. “Electrode Erosion by Particle Ejection in Low-Current Arcs,” J. Appl. Phys. 45 2 1974 667 71
- Gray E. W. Augis J. A. “The Effects of Nanosecond Atmospheric Arcs on Various Metallic Surfaces,” Int. J. Electronics 30 6 1971 533 41
- Germer L. H. “Physical Process in Contact Erosion,” J. Appl. Phys. 29 7 1958 1067 82
- Augis J. A. Gibson F. J. Gray E. W. “Plasma and Electrode Interactions in Short Gap Discharge in Air,” Int. J. Electronics 30 4 1971 315 32
- Gray E. W. Pharney J. R. Augis J. A. “Cathodic Contact Erosion Due to Short-Duration Gas Breakdown Arcs,” J. Phys. D Appl. Phys. 5 1972 1068 76
- Hopkins M. R. Watkins D. H. “The Experimental Study of the Geometry of Erosion Patterns in Platinum Contacts,” Electrical Contact 1972 407 12
- Tenney D. R. Young C. T. Herring H. W. “Oxidation Behavior of TD-NiCr in a Dynamic High Temperature Environment,” Met. Trans. 5 1974 1001 12
- Young C. T. Tenney D. R. Herring H. W. “Dynamic Oxidation Behavior of TD-NiCr Alloy with Different Surface Pretreatments,” Met. Trans. 6A 1975 2253 65