Tooling Effects on Edge Stretchability of AHSS in Mechanical Punching
Technical Paper
2019-01-1086
ISSN: 0148-7191, e-ISSN: 2688-3627
This content contains downloadable datasets
Annotation ability available
Sector:
Language:
English
Abstract
Edge stretchability reduction induced by mechanical trimming is a critical issue in advanced high strength steel applications. In this study, the tooling effects on the trimmed edge damage were evaluated by the specially designed in-plane hole expansion test with the consideration of three punch geometries (flat, conical, and rooftop), three cutting clearances (6%, 14%, and 20%) and two materials grades (DP980 and DP1180). Two distinct fracture initiation modes were identified with different testing configurations, and the occurrence of each fracture mode depends on the tooling configurations and materials grades. Digital Image Correlations (DIC) measurements indicate the materials are subject to different deformation modes and the various stress conditions, which result in different fracture initiation locations. Based on the comparison of hole expansion ratios (HER), the rooftop punch produced the mostly damaged hole with the lowest HER, and failure mode was dominated by edge fracture.
Recommended Content
Authors
Citation
Pu, C., Schmid, K., Wu, W., Makrygiannis, P. et al., "Tooling Effects on Edge Stretchability of AHSS in Mechanical Punching," SAE Technical Paper 2019-01-1086, 2019, https://doi.org/10.4271/2019-01-1086.Data Sets - Support Documents
Title | Description | Download |
---|---|---|
Unnamed Dataset 1 | ||
Unnamed Dataset 2 | ||
Unnamed Dataset 3 |
Also In
References
- Pu , C. and Gao , Y. Crystal Plasticity Analysis of Stress Partitioning Mechanisms and Their Microstructural Dependence in Advanced Steels J. Appl. Mech. 82 3 031003 2015 10.1115/1.4029552
- Shih , H.-C. , Zhou , D. , and Konopinski , B. Effects of Punch Configuration on the AHSS Edge Stretchability SAE Int. J. Engines 10 2017 2051 2056
- Pathak , N. , Butcher , C. , and Worswick , M. Assessment of the Critical Parameters Influencing the Edge Stretchability of Advanced High-Strength Steel Sheet J. Mater. Eng. Perform. 25 11 4919 4932 2016 10.1007/s11665-016-2316-9
- Erdogan , M. The Effect of New Ferrite Content on the Tensile Fracture Behaviour of Dual Phase Steels J. Mater. Sci. 37 17 3623 3630 2002
- Uthaisangsuk , V. , Prahl , U. , and Bleck , W. Modelling of Damage and Failure in Multiphase High Strength DP and TRIP Steels Eng. Fract. Mech. 78 3 469 486 2011 10.1016/j.engfracmech.2010.08.017
- Pu , C. , Gao , Y. , Wang , Y. , and Sham , T.L. Diffusion-Coupled Cohesive Interface Simulations of Stress Corrosion Intergranular Cracking in Polycrystalline Materials Acta Mater. 2017 10.1016/j.actamat.2017.06.058
- Mori , K. , Abe , Y. , Kidoma , Y. , and Kadarno , P. Slight Clearance Punching of Ultra-High Strength Steel Sheets Using Punch Having Small Round Edge Int. J. Mach. Tools Manuf. 65 41 46 2013 10.1016/j.ijmachtools.2012.09.005
- Wu , X. , Bahmanpour , H. , and Schmid , K. Characterization of Mechanically Sheared Edges of Dual Phase Steels J. Mater. Process. Technol. 212 6 1209 1224 2012 10.1016/j.jmatprotec.2012.01.006
- Matsuno , T. , Sato , K. , Okamoto , R. , Mizumura , M. , and Suehiro , M. Synergy Effect of Shear Angle and Anisotropic Material Ductility on Hole-Expansion Ratio of High-Strength Steels J. Mater. Process. Technol. 230 167 176 2016 10.1016/j.jmatprotec.2015.10.018
- Pu , C. , Jia , Y. , Zhou , D. , Makrygiannis , P. et al. Effects of Punch Shapes and Cutting Configurations on the Dimensional Accuracy of Punched Holes on an AHSS Sheet SAE Technical Paper 2018-01-0800 2018 10.4271/2018-01-0800
- Pu , C. , Zhou , D. , Makrygiannis , P. , Wu , W. et al. A Comprehensive Study of Hole Punching Force for AHSS SAE Technical Paper 2018-01-0802 2018 10.4271/2018-01-0802
- Takahashi , Y. , Kawano , O. , Horioka , S. , and Ushioda , K. Improvement of Stretch Flangeability of High-Tensile-Strength Steel Sheets by Piercing under Tension Using Humped Bottom Punch SAE Technical Paper 2013-01-0609 2013 10.4271/2013-01-0609
- Chiriac , C. and Shi , M.F. Experimental Study of Edge Stretching Limits of DP980IBF Steel in Multistage Forming Process SAE Int. J. Mater. Manuf. 8 2 415 418 2015 10.4271/2015-01-0525
- Levy , B.S. and Tyne , C.J. Van 10.1007/s11665-008-9218-4
- Shih , H.-C. , Chiriac , C. , and Shi , M.F. The Effects of AHSS Shear Edge Conditions on Edge Fracture 2010 10.1115/MSEC2010-34062
- Mori , K.i. , Abe , Y. , and Suzui , Y. Improvement of Stretch Flangeability of Ultra High Strength Steel Sheet by Smoothing of Sheared Edge J. Mater. Process. Technol. 210 653 659 2010 10.1016/j.jmatprotec.2009.11.014
- Wu , W. , Wang , Y.W. , Makrygiannis , P. , Zhu , F. et al. Deformation Mode and Strain Path Dependence of Martensite Phase Transformation in a Medium Manganese TRIP Steel Mater. Sci. Eng. A 711 November 2017 611 623 2018 10.1016/j.msea.2017.11.008
- Li , Y. and Wierzbicki , T. Prediction of Plane Strain Fracture of AHSS Sheets with Post-Initiation Softening Int. J. Solids Struct. 47 17 2316 2327 2010 10.1016/j.ijsolstr.2010.04.028
- Bai , Y. and Wierzbicki , T. Application of Extended Mohr-Coulomb Criterion to Ductile Fracture Int. J. Fract. 161 1 1 20 2010 10.1007/s10704-009-9422-8