Mechanical Properties and Collision Deformation Performance of 980 MPa-grade High-Strength Steel Sheet
Technical Paper
2018-01-0624
ISSN: 0148-7191, e-ISSN: 2688-3627
This content contains downloadable datasets
Annotation ability available
Sector:
Language:
English
Abstract
This report describes the mechanical properties, formability, weldability, and collision deformation performance of the new 980 MPa-grade steel sheet used in the front side frame of an automobile’s body framework. In order to determine the material properties of the 980 MPa-grade steel sheet needed for use in the front side frame, the study used special bending tests to find the threshold values at which cracking occurred during collision deformation. It was found that these special bending characteristics correspond closely to hole-expansion properties and it is necessary to increase hole-expansion properties of the new 980 MPa-grade steel sheet. The new 980 MPa-grade steel sheet with high hole-expansion properties has an enhanced forming limit curve compared to conventional 980 MPa-grade steel sheet, and can be formed to the shape of the front side frame. In collapse tests simulating collision deformation, the steel sheets demonstrated the necessary performance without cracking. The new material makes it possible to use 980 MPa-grade steel sheet for components such as the front side frame of an automobile’s body framework, which are challenging to form and undergo significant deformation in collisions.
Recommended Content
Authors
Citation
Maki, H. and Takaki, N., "Mechanical Properties and Collision Deformation Performance of 980 MPa-grade High-Strength Steel Sheet," SAE Technical Paper 2018-01-0624, 2018, https://doi.org/10.4271/2018-01-0624.Data Sets - Support Documents
Title | Description | Download |
---|---|---|
Unnamed Dataset 1 | ||
Unnamed Dataset 2 | ||
Unnamed Dataset 3 |
Also In
References
- Hikida , K. , Nishibata , T. , Suzuki , T. , and Nakayama , N. Development of TS1800MPa Grade Hot Stamping Steel Sheet Materia Japan 52 2 68 70 2013 10.2320/materia.52.68
- Okitsu , Y. , Naito , T. , Takaki , N. , Sugiura , T. et al. Mechanical Properties and Crash Worthiness of Ultrafine Grained Multi-Phase Steel Sheets for Automotive Body Applications SAE Int. J. Mater. Manuf. 3 1 237 245 2010 10.4271/2010-01-0438
- Japan Deep Drawing Research Group Handbook on Sheet Metal Forming Severity Third Tokyo The Nikkan Kogyo Shimbun, Ltd. 2007 79 142 978-4-526-05830-1
- Japan Industrial Standards 2011
- Japan Industrial Standards 2010
- Japan Industrial Standards 2014
- Yamazaki , K. , Mizuyama , Y. , Oka , M. , and Tokunaga , Y. Influence of Microstructure on Bendability of Ultrahigh-Strength Steel Sheet-Formability of Ultrahigh-Strength Steel Sheet Journal of the JSTP 36 416 973 978 1995
- Ishiguro , T. , Yoshida , Y. , Yukawa , N. , Ishikawa , T. et al. Influence of Microstructure on Ductile Damage Behavior of Dual Phase Steel Tetsu-to-Hagane 97 3 136 142 2011
- Japan Deep Drawing Research Group Handbook on Sheet Metal Forming Severity Third Tokyo The Nikkan Kogyo Shimbun, Ltd. 2007 978-4-526-05830-1