Stress Intensity Factor Solutions for Dissimilar Welds in Lap-Shear Specimens of Steel, Magnesium, Aluminum and Copper Sheets
Journal Article
2015-01-1754
ISSN: 1946-3979, e-ISSN: 1946-3987
Sector:
Topic:
Citation:
Lai, W. and Pan, J., "Stress Intensity Factor Solutions for Dissimilar Welds in Lap-Shear Specimens of Steel, Magnesium, Aluminum and Copper Sheets," SAE Int. J. Mater. Manf. 8(2):563-577, 2015, https://doi.org/10.4271/2015-01-1754.
Language:
English
References
- Franklin T. Fatigue behavior and life estimation for dissimilar ultrasonic welds in lap-shear specimens of magnesium and galvanized steel sheets [dissertation] Ann Arbor (MI) University of Michigan 2013
- Sripichai K. , Asim K. , and Pan J. Stress intensity factor solutions for estimation of fatigue lives of laser welds in lap-shear specimens Engineering Fracture Mechanics 78 1424 40 2011
- Zhang S. Stress intensities derived from stresses around a spot weld International Journal of Fracture 99 239 57 1999
- Tran V.-X. , Pan J. Analytical stress intensity factor solutions for resistance and friction stir spot welds in lap-shear specimens of different materials and thicknesses Engineering Fracture Mechanics 77 2611 39 2010
- Suo Z. and Hutchinson W. Interface crack between two elastic layers International Journal of Fracture 43 1 18 1990
- Rice R. and Sih C. Plane problems of cracks in dissimilar media Journal of Applied Mechanics 32 418 23 1965
- Rice R. Elastic fracture mechanics concepts for interfacial cracks Journal of Applied Mechanics 55 98 103 1988
- ABAQUS v6.12 user manual 2012
- Shih F. and Asaro J. Elastic-plastic analysis of cracks on bimaterial interfaces: part I-small scale yielding Journal of Applied Mechanics 55 299 316 1988
- Erdogan F. Stress distribution in a nonhomogeneous elastic plane with cracks Journal of Applied Mechanics 30 232 6 1963
- Lai , W. , Sung , S. , Pan , J. , Guo , Y. et al. Failure Mode and Fatigue Behavior of Dissimilar Laser Welds in Lap-Shear Specimens of Aluminum and Copper Sheets SAE Int. J. Mater. Manf. 7 3 706 710 2014 10.4271/2014-01-1986
- Asim , K. , Sripichai , K. , and Pan , J. Fatigue Failure of Laser Welds in Lap-Shear Specimens of High Strength Low Alloy (HSLA) Steels under Cyclic Loading Conditions SAE Int. J. Mater. Manuf. 4 1 571 580 2011 10.4271/2011-01-0473
Cited By
Recommended Content
Technical Paper | Stresswave® Fatigue Life Improvement Process |
Technical Paper | Crush Characteristics of AA6061-T6 Round Tubes During a Cutting Deformation Mode |
Technical Paper | Dynamic Denting of Autobody Panels |