Gaskets for Extreme Exhaust Test Applications
ISSN: 0148-7191, e-ISSN: 2688-3627
Published April 14, 2015 by SAE International in United States
Annotation ability available
Gasket materials are utilized for various different types of high temperature testing to prevent leaking at bolted joints. In particular, the automotive test services field uses flanged-gasket bolted exhaust joints to provide a convenient method for installation & removal of exhaust components like catalytic converters for aging, performance testing, etc. Recent improvements in the catalyst aging methods require flanged-gasket joints that can withstand exhaust temperatures as high as 1200°C. Gasket materials previously used in these applications like the graphite based gasket materials have exhibited physical breakdowns, severe leakage, and general thermal failures under these extreme temperatures. In order to prevent these leaks, metal-reinforced gasket materials in a number of configurations were introduced to these extreme temperature environments to evaluate their robustness to these temperatures. A series of experiments were implemented to evaluate different flange and gasket material in this extreme test environment. The variables evaluated are as followed: gasket material, gasket thickness, flange material, and flange thickness. Responses evaluated were: reusability, effectiveness of seal pre/post exposure measured via cold leak rates, and the general robustness of the materials to these extreme temperatures. It was determined from this testing that in order to meet the desired leak requirements of 0.5 Lemail@example.comKPa[5 psig] that 12.7 mm [½″] thick 304 stainless steel flanges and HT400 (0.080″) gasket materials would provide the best flange-gasket combination for overall robustness to extreme catalyst aging.
|Ground Vehicle Standard||Sintered Carbide Tools|
|Technical Paper||Laboratory Testing of Cabin Air Filters for the Removal of Reduced-Sulfur Odors|
|Technical Paper||Comparison of Air Filtration Efficiency Measurements for Pleated and Flat Sheet Filters|
CitationRichmond, K., Henry, S., Richmond, R., and Belton, D., "Gaskets for Extreme Exhaust Test Applications," SAE Technical Paper 2015-01-1740, 2015, https://doi.org/10.4271/2015-01-1740.
- GM Statement of Requirements, REV 11.
- AR400 Product Specifications Sheet
- HT400 Product Specifications Sheet
- HT514 Product Specifications Sheet