Improvement of Stretch Flangeability of High-Tensile-Strength Steel Sheets by Piercing under Tension Using Humped Bottom Punch
Technical Paper
2013-01-0609
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
To meet the requirements for weight reduction of automobiles, high-tensile-strength steel sheets have been applied extensively to the manufacture of auto parts. But their relatively lower press formability has been obstructing their further application, and so it is recommended that the stretch flangeability of such steel sheets be increased, and cracks that occur when stretching the edges during the press forming of such steel sheets be suppressed. Thus the authors have conducted a study to improve the stretch flangeability of high-tensile-strength steel sheets by optimizing the punching method and obtained the following conclusion.
Work hardening beneath the pierced edge is mainly caused by deformation due to the punch motion while it is shearing the material. By attaching a hump of a certain shape at the bottom of the punch, ductile fracture in the material adjacent to the punch corner is accelerated by the hump's effect to increase stress triaxiality, which reduces the extent of total deformation which takes place during the shearing process, thereby improving the stretch flangeability of the material.
Recommended Content
Authors
Citation
Takahashi, Y., Kawano, O., Horioka, S., and Ushioda, K., "Improvement of Stretch Flangeability of High-Tensile-Strength Steel Sheets by Piercing under Tension Using Humped Bottom Punch," SAE Technical Paper 2013-01-0609, 2013, https://doi.org/10.4271/2013-01-0609.Also In
References
- Nakagawa T. , Yoshida K. Rikagaku-kennkyuusho-houkoku 44-2 1968 91 105
- Nakagawa T. , Yoshida K. Rikagaku-kennkyuusho-houkoku 44-3 1968 150 162
- Iwaya J. , Okano Y. , Ueno K. Kobe Steel Engineering Report 47-2 1997 33 37
- Japanese Society of Technology and Plasticity Sen-dan-kakou 2000 87 Corona Publishing Co.Ltd.
- Japanese Society of Technology and Plasticity Sen-dan-kakou 2000 11 Corona Publishing Co.Ltd.
- Hancock , J.W. , Mackenzie , A.C. Journal of the Mechanics and Physics of Solids 24-2 1976 147 160
- Shimanuki H. , Huruya H. , Inoue T. , Hagiwara Y. , Toyata M. Nihon Zousen Gakkai Ronbunshuu 186 1999 475 483
- Yoshinari H. , Enami K. , Kan M. , Kaneda S. J. Soc. Mat., Japan 54-3 2005 296 301