Effect of Chemical Composition on Tensile Property in TRIP-assisted Multiphase Steel Composed of Fe-Mn-Si-C
Technical Paper
2007-01-3728
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
The microstructural changes and the tensile properties of the TRIP-assisted steels resulting from the different chemical compositions were investigated by using SEM, TEM, XRD and UTM. As a result of microscopic observation, morphology of retained austenite could be identified into two types: a granular type in steel containing higher Si and a film type in steel having higher C. In the case of the steel containing higher C with a tensile strength of 860 MPa and a total elongation of 38 %, the film-typed retained austenite could be observed among the lath bainitic ferrites. Actually, the metastable retained austenite was the requisite for the good formability, which means that the chemical composition plays a significant role in the microstructure and the tensile property of a TRIP-assisted steel. Regarding the tensile property, each steel containing adequate amount of Si and Mn showed a typical TRIP effect on a stress-strain curve while the steel containing a higher Mn content exhibited the similar behaviors shown in the dual phase steels.
Authors
Topic
Citation
Lee, K., Bang, I., Lee, S., and Choi, S., "Effect of Chemical Composition on Tensile Property in TRIP-assisted Multiphase Steel Composed of Fe-Mn-Si-C," SAE Technical Paper 2007-01-3728, 2007, https://doi.org/10.4271/2007-01-3728.Also In
References
- Zackay V. F. Parker E. R. Busch R. 1967 Enhancement of Ductility in Steels Trans. ASM 113 321 350
- Sakuma Y. Matsumura O. Takechi H. 1991 Mechanical Properties and Retained Austenite in Intercritically Heat Treated Bainite Transformed Steel Met. Trans. 22A 489
- Krauss G. 1989 Steels : heat treatment processing principles MASM International, OH, USA 78 80
- Matsumura O. Sakuma Y. Takechi H. 1987 Enhancement of Elogation by Retained Austenite in Intercritical Annealed 0.4C-1.5Si-0.8Mn Steel Trans ISIJ 27 570
- Liu S. K. Zhang J. 1990 The Kinetics of the Bainite Transformation Met. Trans. 21A 1517
- Jacques P. Girault E. van Humbeeck J. Aernoudt E. Delannay F. 1997 Experiment Characterization of the Bainitic Transformation Kinetics Journal de Physique IV 459
- Chen H. C. Era H. Shimizu M. 1989 Effect of Phosphorus on Formation of Retained Austenite and Mechanical Property in Si-containing Steels Met. Trans. 20A 437
- Bhadeshia H.K. D. H. Edmonds D. V. 1980 Bainite in Silicon Steels MActa Metall. 28 1265