Deformation and Texture Behaviors of Al-3mass%Mg Alloy at High Temperatures
Technical Paper
2003-01-2786
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
Uniaxial compression tests were conducted on Al-3mass%Mg alloy under various temperatures and true strain rates. High temperature yielding was observed at the temperatures higher than 623K. Texture examination elucidated that fiber textures are constructed in all the deformation conditions examined in this study. It was found that the kinds and the intensities of texture components varied depending on deformation temperature, strain rate and the amount of strain.
It was concluded that orientation stability against the lattice rotation by slip deformation as well as the rapid recovery during the deformation of the grains close to {001} orientation made it possible to grow by consuming the other deformed grains with the orientations such as {011}, resulting in the development of {001} texture.
Authors
Citation
Okayasu, K. and Fukutomi, H., "Deformation and Texture Behaviors of Al-3mass%Mg Alloy at High Temperatures," SAE Technical Paper 2003-01-2786, 2003, https://doi.org/10.4271/2003-01-2786.Also In
References
- Otsuka M. Horiuchi R. J. Japan Inst. Metals 36 1972 809 817
- Chen S. R. Kocks U. F. Hot Deformation of Aluminum Alloys Langdon T. G. et al. The Minerals, Metals and Materials Society 1991 89 104
- Knutsen R. D. Humphreys F. J. Bate P.S. Court S. A. Proceedings of the 12th International conference on Textures of Materials 1999 617 622
- Horiuchi R. Yoshinaga H. Hama S. Trans. Japan Inst. Metals 6 1965 123 130
- Cottrell A. H. Jaswon M. A. Proc. R. Soc. A 199A 1949 104 114
- Abstracts of the 132nd Annual Meeting of the Japan Institute of Metals 2003 447
- Humphreys F. J. Hatherly M. Recrystallization and Related Annealing Phenomena Pergamon, Oxford 1995 373
- Horiuchi R. Otsuka M. Trans. Japan Inst. Metals 13 1972 284 293
- Kocks U. F. Chen S. R. Dawson P. R. Materials Science Forum 157-162 1797 1802
- Tagami M. Kashihara K. Okada T. Inoko F. Trans. Japan Inst. Metals 42 2001 2013 2020
- Fukutomi H. Nomoto A. Osuga Y. Ikeda S. Mecking H. Analysis of Dynamic Recrystallization Mechanism in γ -TiAl Intermetallic Compound based on Texture Measurement Intermetallics 1996 s49 s54