Correlation between Accelerated Laboratory Tests and Field Tests for Filiform Corrosion of Painted Aluminum Alloy Sheets for Automobiles
Technical Paper
2003-01-2749
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
Correlation between accelerated laboratory tests and field tests for filiform corrosion of painted aluminum alloy sheets for automobile was investigated by conducting six kinds of laboratory tests with different pH, dry-wet condition, etc., and two sites of outdoor exposure tests, and vehicle test. It was found that susceptibility to filiform corrosion in the laboratory tests increased with the decrease of pH and/or the increase of repetition rate of wet/dry cycle. The susceptibility in the laboratory tests also increased with the increase of Cu contents in the alloy or with the sanding treatment before painting. The same tendency was obtained in the outdoor exposure tests and vehicle test. However, the correlation of the outdoor exposure tests and the vehicle test was low. In conclusion, the laboratory tests with relatively low wet ratio (70%) correlated well with the outdoor exposure tests, and the tests with relatively high wet ratio (95%) correlated well the vehicle tests.
Recommended Content
| Aerospace Material Specification | Aluminum Alloy, 2024, Bar, Rod, and Wire; Rolled, Drawn, or Cold Finished |
| Aerospace Material Specification | Brass, Seamless Tubing 66.5Cu - 31.5Zn - 1.6Pb Drawn Temper (H58) |
| Aerospace Material Specification | Titanium Alloy Bars, Forgings, and Forging Stock 6.0Al - 2.0Sn - 4.0Zr - 6.0Mo Solution Heat Treated and Aged |
Authors
Topic
Citation
Nakayama, T., Shige, H., Vega, L., and Colvin, E., "Correlation between Accelerated Laboratory Tests and Field Tests for Filiform Corrosion of Painted Aluminum Alloy Sheets for Automobiles," SAE Technical Paper 2003-01-2749, 2003, https://doi.org/10.4271/2003-01-2749.Also In
References
- Matuso K. et al Alutopia 8 1992 55
- Ikeda K. et al Materia Japan 34 1995 801
- Colvin E.L. et al SAE 970735 1997 69
- Shige H. et al J.Mat. Sci. JPN 49 2000 1193
- Slabough W.H. et al J.R.T. 44 1992 76
- Van.Loo M. et al Corrosion 9 1953 277