Microstructure and Dimensional Stability in Si-Mo Ductile Irons for Elevated Temperature Applications
Technical Paper
2002-01-2115
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
The demands for high temperature metallic applications requires increased thermal (i.e., microstructural and dimensional) stability due to ever tightening tolerances, restrictive designs and higher Internal Combustion Engine (ICE) operating temperatures. Furthermore, these demands have caused the industry to place restrictive microstructure specifications on ductile iron production to ensure dimensional stability for certain applications. The presence of a distribution of precipitate phase was identified in Si-Mo iron as that with the Fe2MoC-type structure, or less predominantly with a two-phase Fe2MoC/M6C-type structure, which is often mistaken for pearlite. This structure may provide Si-Mo irons with an inherent microstructure advantage with respect to dimensional stability at elevated temperatures, relative to alternative ductile iron materials containing a pearlitic microstructure. This paper describes the results of the microstructural characterization of a Si-Mo ductile iron and its influence on the thermal stability of this material. Complete microstructure analysis, semi-quantitative chemical analysis and dilatometer results have shown the absence of pearlite and the existence of a more thermally stable moly-rich precipitate distribution.
Recommended Content
Authors
Topic
Citation
Black, B., Burger, G., Logan, R., Perrin, R. et al., "Microstructure and Dimensional Stability in Si-Mo Ductile Irons for Elevated Temperature Applications," SAE Technical Paper 2002-01-2115, 2002, https://doi.org/10.4271/2002-01-2115.Also In
References
- Sponseller D.L., Scholz W.G., Rundle D.F., “Development of Low-Alloy Ductile Irons For Service at 1200-1500F”, AFS Transactions, Vol 76, 1968.
- Fairhurst, W. and Roehrig, K., “High-silicon Nodular Irons” Foundry Trade Journal, March 29, 1979.
- Lyman, T., Troiano, A.R., “Influence of Carbon Content upon the Transformations in 3 Per Cent Chromium Steel,” Transactions ASM, vol. 37, p. 402 (1946).
- Gilbert, G.N.J., “The Growth and Scaling Characteristics of Cast Irons in Air and Steam” BCIRA J. v.7, n. 10, pp. 478-566, 1959.
- Roehrig K., “Thermal Fatigue of Gray and Ductile Irons”, AFS Transactions, vol. 78-02, p75-88 (1978).
- Fredriksson H. and Sterndahl J., “Solidification of iron-base alloys”, Metal Science, vol. 16, pp. 575-585. 1982.
- Metals Handbook 8th edition, Vol.8 - Metallography, Structure and Phase Diagrams, ASM, 1973.
- Skaland, T., Elkem ASA Research, personal communication, February 2002.
- Goodhew P., Specimen Preparation in Materials Science, Elsevier, p. 154.
- Andrews K.W., Dyson D.J. and Keown S.R., Interpretation of Electron Diffraction Patterns, 2nd ed., Adam Hilger Ltd. (1971).
- Hume-Rothery W., The Structures of Alloys of Iron, Pergamon Press (1966).
- Shtansky D.V. and Inden G., Acta Mater., vol. 45, no. 7, pp. 2879-2895 (1997).
- Raynor G.V. and Rivlin V.G., Phase Equilibria in Iron Ternary Alloys, The Institute of Metals (1988), pp. 398-413.
- Loretto M.H., Electron Beam Analysis of Materials, 2nd ed., Chapman & Hall (1994), pp. 71-74.