Effects of Alloying Elements on Mechanical Properties and Phase Transformation of TRIP Cold Rolled Steel Sheets
Technical Paper
2000-01-2699
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
Tensile and dilatation tests were conducted in order to study the effects of Mn, Si and Nb on the transformation behavior in the 0.14C - (2.1∼2.4)Mn - (0.5∼1.0)Si (0.00∼0.02)Nb TRIP steels. The volume fraction of bainite transformed during austempering, ΔVB, and the martensite start temperature, Ms, were measured. ΔVB was dependent on the austempering temperature and a minimum in ΔVB was obtained at 450°C for all the examined steels. Ms temperature was linearly decreased as ΔVB was increased. The ratio of Ms decrease to ΔVB was not dependent on the composition of steels, but on the austempering temperature, exhibiting a maximum when the austempering temperature was 450°C. It was also observed that elongation was the greatest when the ratio was maximum. Ms was increased when the amount of Mn was increased from 2.1% to 2.4%. It was because Mn retarded the ferrite transformation rate so that the soluble C diffused from the ferrite to the austenite was decreased. The addition of Si decreased Ms because it activated the diffusion of C to austenite during the cooling to the austempering temperature. The addition of Nb was observed to give little influence on ΔVB and the Ms.
Recommended Content
Authors
Topic
Citation
Baik, S., Kim, S., Jin, Y., and Kwon, O., "Effects of Alloying Elements on Mechanical Properties and Phase Transformation of TRIP Cold Rolled Steel Sheets," SAE Technical Paper 2000-01-2699, 2000, https://doi.org/10.4271/2000-01-2699.Also In
References
- Zackay V.F. Parker E.R. Fahr D. Busch R. Trans. ASM. 60 1967 252
- Olson G.B. Cohen M. Metall. Trans. 7A 1976 1897
- Sugimoto K. Usui N. Kobayashi M. Hashimoto S. ISIJ 32 1992 1311
- Matumura Sakuma Y. Takechi H. Trans. ISIJ 27 1987 571
- Sakuma Y. Matumura O. Takechi H. Metall. Trans. 22A 1991 489
- Bhadeshia H.K.D.H. Edomonds D.V. Metall. Trans. 10A 1979 895
- Bai D.Q. Chiro A.D. Yue S. Materials Science Forum 284-286 1998 253
- Bleck W. Hulka K. Papamentellos K. Materials Science Forum 284-286 1998 327
- Chen H.C. Era H. Shimizu M. Metallur. Trans. 20A 1987 437
- Hanzaki A. Zatei hodgson P.D. Yue S. ISIJ, Int. 35 1995 79
- Speich G.R. Demarest V.A. Miller R.L. Metall. Trans. 12A 1981 1419
- Davies R.G. Metall. Trans. 10A 1979 113
- Jaffe L.D. Hollomon u.I.H. Trans. AIME 167 1946 617
- Tsukatani I. Hashimoto S. Inoue T. ISIJ Int. 31 1991 992
- Takahashi M. Bhadeshia H.K.D.H. Materials Trans. JIM 32 1991 689
- Matsumura O. Sakuma Y. Takechi H. Transactions ISIJ 27 1987 571
- Owen W.S. Trans. Am. Soc. Mat. 46 1954 812
- Thomas G. Koo J-Y “Structure and Properties of Dual Phase Steels” New Orleans TMS/AIME 1979 183