430LNb - A New Ferritic Wire for Automotive Exhaust Applications
Technical Paper
2000-01-0314
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Event:
SAE 2000 World Congress
Language:
English
Abstract
The increasing use of ferritic stainless steels (AISI 409, 439, 436 and 441) in automotive exhaust systems, especially for manifolds and catalytic converter canning, has led the authors to develop a new ferritic welding wire, designated 430LNb. This new material is recommended for the GMAW and GTAW processes and provides better metallurgical compatibility with the ferritic base metals, in terms of both thermal expansion and microstructure.
The composition of the new welding wire has been adjusted in order to guarantee an entirely ferritic structure in the welds of ferritic sheet materials, together with good resistance of the welds to both wet corrosion and high temperature oxidation, corresponding to the conditions encountered respectively in the colder and hotter parts of the exhaust line. This is achieved by limitation of the C (<0.02%) and N (<0.02%) contents, stabilisation with Nb, such that Nb > 0.05 + 7 (C + N) and Nb < 0.5%, and a Cr content of 17.8-18.8%.
GMAW weldability tests on 1 and/or 1.5 mm thick sheets of AISI 409, 436 and 441 grades, using 1 mm diameter 430LNb welding wire, gave good quality beads (shape, structure, tensile properties, bending, intergranular corrosion resistance), with a welding speed of the order of 2 m/min. The quality of the weld seams obtained was at least as good as that of welds made on the same sheets using austenitic filler materials (308LSi and 307Si). Tests specific to the automotive exhaust application have been undertaken in the laboratory in order to compare the service behaviour of the welds with that obtained using austenitic filler wires. These included fatigue endurance tests performed in the tension-compression mode between 300 and 950°C, thermal fatigue tests involving cycling of restrained specimens between 250 and 900°C, and dip-dry corrosion-oxidation tests simulating the combination of salt attack and high temperature corrosion. All the results obtained confirm that the 430LNb welding wire is at least as good as the austenitic filler materials most commonly employed in Europe. Tests carried out on real components by exhaust system manufacturers also confirm the high productivity and good quality of the welds.
Recommended Content
Authors
Citation
Renaudot, N., Santacreu, P., Ragot, J., Moiron, J. et al., "430LNb - A New Ferritic Wire for Automotive Exhaust Applications," SAE Technical Paper 2000-01-0314, 2000, https://doi.org/10.4271/2000-01-0314.Also In
References
- DEVINE T.M. DRUMMOND J. ‘An Accelerated Intergranular Corrosion Test for Detecting Sensitization in Low Chromium Ferritic Stainless Steel’ in Corrosion NACE 38 6 1982
- SASSOULAS H. SANTACREU P-O. ‘Eléments pour prédire la durée de vie en fatigue thermique d'élements de lignes d'échappement réalisés en acier inoxydable’ 18 ème Journée de Printemps de la SF2M- Dimensionnement en Fatigue des Structures: Démarche et outils Paris 2-3 June 1999 161
- SANTACREU P-O. et al. ‘Thermal Fatigue of Stainless Steels and its Application to Life Prediction of Automotive Exhaust Lines’ Thermal Stresses'99 Cracow, Poland June 13-17 1999 245