Analysis of Surface Morphology Change Due to Forming of Zinc-Coated Sheet Steels for Automotive Panel Applications
Technical Paper
2000-01-0310
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Event:
SAE 2000 World Congress
Language:
English
Abstract
A three-dimensional surface profilometer has been used to examine the surface morphology in various regions of stamped automotive steel parts. This analysis provides insight into the nature of the surface morphology development during stamping. For this work, four stamped zinc-coated sheet steel sections were considered. Each of the sections was examined with the 3-D surface profilometer in a variety of regions suspected to show different surface morphology due to differences in forming. Upon analysis of the surface height frequency histograms, different modes of deformation on the part surface were identified and categorized. Three modes of surface deformation were observed - “simple pressing”, “pressing with small scale sliding and bending” and “pressing with gross sliding, stretching and bending”. Each mode had a distinctive set of characteristics in the frequency height histograms. These modes were observed in both galvannealed steel sheet and hot-dipped galvanized steel sheet. From the surface morphology development, frictional effects can be hypothesized.
Recommended Content
Technical Paper | Objective Testing in Handling Research |
Technical Paper | High-Strength Steel for Cost Effective Weight Reduction |
Technical Paper | Formability of TS590 N/mm2 “Tri-Phase” Hot Rolled Steel |
Authors
Citation
Wichern, C., Van Tyne, C., and Belanger, P., "Analysis of Surface Morphology Change Due to Forming of Zinc-Coated Sheet Steels for Automotive Panel Applications," SAE Technical Paper 2000-01-0310, 2000, https://doi.org/10.4271/2000-01-0310.Also In
References
- Ren N. Lee S.C. “The Effects of Surface Roughness and Topography on the Contact Behavior of Elastic Bodies” Transactions of the ASME 116 1994 804 811
- Miura K. Hira T. Furukimi O. Obara T. “Zinc Coated Steel Sheets with Superior Press Formability and Image Clarity” Proceedings of the 37 th Mechanical Working and Steel Processing Conference 33 ISS Warrendale, PA 1996 173 178
- Meuleman D.J. Dwyer T.E. “Die Materials and Treatments with Electrogalvanized Steels” SAE Technical Paper 880369 1988
- Dalton Schey J.A. “Effect of Bead Finish Orientation on Friction and Galling in the Drawbead Test” SAE Technical Paper 920632 1992
- Schey J.A. “Solid Film Lubrication of Galvanized Steels” SAE Technical Paper 950697 1995
- Coubrough G. “Friction During Stretch-Bend Forming” Ph.D. Thesis Colorado School of Mines Golden, CO 1998