Investigation of a Failed Shock Strut Mount from an AH-64 Apache Helicopter
Technical Paper
1999-01-1421
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
ABSTRACT
The US Army Research Laboratory performed a failure investigation on a broken main landing gear mount from an AH-64 Apache attack helicopter. This “infinite-life” component had failed in flight, and initially prevented the helicopter from safely landing. In order to avoid a catastrophe, the pilot had to perform a low hover maneuver to the maintenance facility, where ground crews assembled concrete blocks at the appropriate height to allow the aircraft to safely touch down. The failed part was fabricated from maraging 300 grade steel (2,068 Mpa [300 ksi] ultimate tensile strength), and was subjected to visual inspection/light optical microscopy, metallography, electron microscopy, energy dispersive spectroscopy, chemical analysis, and mechanical testing. It was observed that the vacuum cadmium coating adjacent to the fracture plane had worn off and corroded in service, thus allowing pitting corrosion to occur. The failure was hydrogen-assisted and was attributed to stress corrosion cracking (SCC) and/or corrosion fatigue (CF). Contributing to the failure was the fact that the material grain size was approximately double the required size, most likely caused from higher than nominal temperatures during thermal treatment. These large grains offered less resistance to fatigue and SCC. In addition, evidence of titanium-carbo-nitrides was detected at the grain boundaries of this material which was prohibited according to the governing specification. This phase is formed at higher thermal treatment temperatures (consistent with the large grains) and tends to embrittle the alloy. It is possible that this phase may have contributed to the intergranular attack. Recommendations were offered with respect to the use of a dry film lubricant over the cadmium coated region, and the possibility of choosing an alternative material with a lower notch sensitivity. In addition, the temperature at which this alloy is treated must be monitored to prevent coarse grain growth. As a result of this investigation and in an effort to eliminate future failures, ARL assisted in developing a cadmium brush plating procedure, and qualified two Army maintenance facilities for field repair of these components.
Recommended Content
Technical Paper | An Advanced Alloy for Landing Gear and Aircraft Structural Applications - Aerometr® 100 Alloy |
Aerospace Standard | Landing Gear Shock Strut Bearing Selection |
Technical Paper | Survey of Candidate Aluminum Materials for Supersonic Aircraft Applications |
Topic
Citation
Pepi, M., "Investigation of a Failed Shock Strut Mount from an AH-64 Apache Helicopter," SAE Technical Paper 1999-01-1421, 1999, https://doi.org/10.4271/1999-01-1421.Also In
References
- Engel L. Klingele, H. “An Atlas of Metal Damage” Prentice-Hall, Inc., New Jersey” 1981 130
- Floreen S. Decker, R.F. “Heat Treatment of 18% Ni Maraging Steel”, Source Book on Maraging Steels” 1979 23
- Birkle, A.J. Dabkowski, D.S. Paulina, J.P. Porter, L.F. “A Metallographic Investigation of the Factors Affecting the Notch Toughness of Maraging Steels”, Source Book on Maraging Steels” 1979 127 130.
- Carter, C.S. “Fracture Toughness and Stress Corrosion Cracking Characteristics of a High Strength Maraging Steel”, Source Book on Maraging Steels” 1979 181
- Kalish D. Rack, H.J. “Thermal Embrittlement of 18 Ni Maraging Steel”, ASM Source Book on Maraging Steels” 1979 37
- Dean, S.W. “Stress Corrosion Cracking Behavior of Maraging Steels in Natural Environments, Corrosion - National Association of Corrosion Engineers” 1964 102
- Stavros A.J. Paxton, H.W. “Stress-Corrosion Cracking Behavior of an 18 Pct. Ni Maraging Steel”, ASM Source Book on Maraging Steels” 1979 179
- Champagne, V.K. Wechsler, G. “Failure Analysis of the Shock Strut Mount Located on the AH-64 Apache Helicopter”, Letter Report 10 May 1991