Effects of Ni, Cu, Si and Co on the Corrosion Properties of Permanent Mould Cast Medallions and Die Cast Plates of Magnesium Alloy AZ91
Technical Paper
1999-01-0926
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
Permanent mould cast medallions and 3mm die cast test plates of 47 different AZ91 based alloys covering 3-129 ppm Ni, 7-2850 ppm Cu, 87-1740 ppm Si and 0-100 ppm Co were produced. Medallions and plates were subjected to 72 hours immersion in 5% NaCl solution at 25C and to the 10 day ASTM-B117 salt spray test. The results include: a) for AZ91, the corrosion rate values anticipated from salt spray testing of die cast test plates can be calculated from the results of immersion tests on permanent mould cast medallions; b) the effect of Co on corrosion of AZ91 is 35-75 times more detrimental than Cu and thus similar to that of Ni; and c) Si showed almost no effect on the corrosion rates in the alloys examined.
Recommended Content
| Technical Paper | Properties of Magnesium Plaster Castings |
| Technical Paper | Aluminum P/M Parts - Their Properties and Performance |
| Technical Paper | Metallurgical Factors Related to Machining Aluminum Castings |
Authors
Citation
Bakke, P., Sannes, S., and Albright, D., "Effects of Ni, Cu, Si and Co on the Corrosion Properties of Permanent Mould Cast Medallions and Die Cast Plates of Magnesium Alloy AZ91," SAE Technical Paper 1999-01-0926, 1999, https://doi.org/10.4271/1999-01-0926.Also In
References
- Pinfold P.M.D. ∅ymo D. “An evaluation of refined, recycled AZ91D alloy” SAE Techn. Paper , 930420 Detroit, MI, US 1993
- Skar J.I. “Paints and coatings used on magnesium” HRE report 95P_CA2.DOC 1995
- Beck A. The technology of magnesium and its alloys F.A. Hughes & Co. Ltd. London, UK 1940
- Hanawalt J.D. Nelson C.E. Peloubet J.A. “Corrosion studies of magnesium and its alloys” Trans. AIME 47 273 299 1942
- Beerwald A. “Über den Einfluß von Verunreinigungen auf die Korrosionseigenschaften des Magnesiums und seiner Legierungen mit Mangan und Aluminium” Z. Metallkunde Januar 28 31 1941
- Hanawalt J.D. Nelson C.E. Holdeman G.E. “Removal of iron from magnesium base alloys” Dec. 30 1941
- Fox F.A. Bushrod C.J. Mayer S.E. “Some factors in the reduction of the iron content of magnesium-base alloys” J. Inst. Met. 73 55 82 1947
- Emley E.F. Principles of magnesium technology Pergamon Press Oxford, UK 1966
- Hillis J.E. “The effect of heavy metal contamination on magnesium corrosion performance” SAE Techn. Paper , 830523 Detroit MI, US 1983 SAE Trans. 92 1983
- Reichek K.N. Clark K.J. Hillis J.E. “Controlling the salt water corrosion performance of magnesium AZ91 alloy” SAE Techn. Paper , 850417 Detroit MI, US 1985
- Hillis J.E. Reichek K.N. “High purity magnesium AM60 alloy: The critical contamination limits and the salt water corrosion performance” SAE Techn. Paper , 860288 Detroit, MI, US 1986
- Hillis J.E. Shook S.O. “Composition and performance of an improved magnsium AS41 alloy” SAE Techn. Paper , 890205 Detroit, MI, US 1989
- Mercer W.E. II Hillis J.E. “The critical contamination limits and salt water corrosion performance of magnesium AE42 alloy” SAE Techn. Paper , 920073 Detroit, MI, US 1992
- Aune T.K. “Minimizing base metal corrosion on magnesium products. The effect of element distribution (structure) on corrosion behavior” 40th IMA Conf. 1983
- Rozak G.A. “Investigation of the quality and corrosion resistance of recycled AZ91D magnesium ingot” SAE Techn. Paper , 940412 Detroit, MI, US 1994
- Steen-Hansen R. “Review of corrosion behaviour of Mg alloys” Intl. conf. on magnesium and their applications Garmisch-Partenkirchen Germany April 8-10 1992
- Lunder O. Aune T.K. Videm M. Nisancioglu K. “Corrosion Resistant Magnesium Alloys” SAE Techn. Paper , 950428 Detroit, MI, US 1995
- Nayeb-Hashemi A.A. Clark J.B. Phase diagrams of binary magnesium alloys ASM Intl. Metals Park, OH, US 1988
- Holta O. Westengen H. Røen J. “High purity magnesium die casting alloys. Impact of metallurgical principles on industrial practice” 3rd Intl. Magnesium Conf. Manchester, UK April 10-12 1996
- Schneider A. Stendel J. “Ausfällung intermetallischer Phasen aus einem flüssigen Lösungsmetall” Z. Anorganische und Allgemeine Chemie 227 246 1960
- Foerster G.S. “Removal of nickel from molten magnesium metal” March 4 1975
- Mohagen M. “Raffinering av ren-magnesium, spesielt med titanforbindelser” Norsk Hydro report, RP334 1959
- Valland G. “Fremstilling av renere magnesium. Delrapport nr. 1, Raffinering med ZrCl 4 ” Norsk Hydro report RP594 1965
- Kolby P. “(Fe,Mn) containing particles in cast and remelted magnesium alloy AZ91” SINTEF Materials Technology report May 1994
- Baker H. ASM Handbook, Vol. 3, Alloy Phase Diagrams ASM Intl. Materials Park, OH, US 1992
- Höllrigl-Rosta F. Just E. Köhler J. Melzer H.J. “Magnesium in Volkswagen” 37th IMA Conf. 38 45 1980
- Zuliani D.J. “Improved corrosion resistance of ultra high purity AZ91 magnesium alloy” Timminco Metals Research Bulletin
- Norsk Hydro Research Centre HRE-MAT-A-38 Procedure “Vekttapsmålinger” 1995
- Norsk Hydro Research Centre HRE-MAT-A-39 Procedure “Korrosjonstest I salttåkekammer” 1996
- MODDE, Ver.3.0 Umetri AB Umeå, Sweden 1995
- Toft J. StrÆm H. “Sammenheng mellom salttåke- og dyppetest anvendt på Mg-legeringer” HRE report 96P_FN5.DOC 1996