Conductive TPO
Annotation ability available
Sector:
Language:
English
Abstract
Conductively modified thermoplastic olefins (TPOs) have been developed using low levels of conductive carbon fillers, <6 wt.%, without sacrificing the favorable mechanical and rheological properties exhibited by these materials for the automotive market. The bulk electrical properties of these materials exhibit traditional percolation behavior when the samples are compression molded. However, conductively modified injection molded materials exhibit a high surface resistivity, typically greater than 1016 ohm cm, which is compensated by a relatively low resistance interior, defined as a core resistance, of less than 109 ohm/cm. The threshold for electrostatic paintability has been identified based on core resistance measurements, electrostatic dissipation results, and electrostatic painting transfer efficiency data. The core resistance must be less that 109 ohm/cm for charge dissipation to occur and for any significant increase in paint film builds to be observed. Electrostatic painting of representative production rear bumper fascias at Visteon - Utica Plant have shown transfer efficiency increases relative to non-conductive parts for adhesion promoter, primer, basecoat, and clearcoat when conductive TPO resins are employed. This is true even with the use of conductive adhesion promoter and primers. Recent advancements in chemistries and processes which eliminate adhesion promoters, such as olefinic topcoats, plasma or flame surface treatments, or directly paintable TPO formulations, are targeted towards cost savings associated with process and/or coating elimination. However, by elimination of conductive surface coatings prior to electrostatic application of basecoat and clearcoat over non-conductive TPO parts, these potential cost savings are more than offset by a loss in painting efficiency. The use of conductive TPO parts enables these promoterless system approaches by maintaining the highest possible transfer efficiency levels in electrostatic painting processes.
Topic
Citation
Helms, J. and Blais, E., "Conductive TPO," SAE Technical Paper 980709, 1998, https://doi.org/10.4271/980709.Also In
References
- a) Garner D. P. Elmoursi A. A. “Electrostatic painting of plastics I: electrical properties of plastics and primers,” J. Coatings Tech. 63 33 37 1991 b) Elmoursi A. A. Garner D. P. “Electrostatic painting of plastics II: electric field effects,” J.Coatings Tech. 64 39 44 1992 c) Elmoursi A. A. “Electrostatic painting of plastics using metal-backing,” IEEE Trans. Industry Applications 29 1053 1057 1993
- Migda F. M. “New methods for evaluating electrostatic paintability of plastics” ASM/ESD Advanced Coatings Conference Chicago, IL Nov. 3-5 1992
- Helms J. Blais E. Cheung M.-F. “Thermoplastic compositions with modified electrical conductivity” January 16 1996
- McDonald J. R. Impedance Spectroscopy: Emphasizing Solid Materials and Systems John Wiley and Sons New York 1987
- Boukamp B. A. Equivalent Circuit Ver. 3.0 Department of Chemical Technology, University of Twente P.O. Box 217, 7500 AE Enschde, The Netherlands 1989
- Migda F. Ford Motor Company Laboratory Test Method
- Helms J. Blais E. Cheung M. Schroeder J. Derengowski T. “Conductive modification of injection molded thermoplastics: electrical properties and electrostatic paintability,” IEEE Industry Applications Conference Record, 30th IAS Annual Meeting 2 1514 1522 1995
- Stauffer D. Introduction to Percolation Theory Taylor and Francis Philadelphia 1985
- Cheung M.-F. Bauer D. R. “Thermal characterization of thermoplastic polyolefins,” Ford Motor Company Technical Report #: SR-93-151
- a) Sumita M. Sakata K. Hayakawa Y. Asai S. Miyasaka K. Tanemura M. “Double percolation effect on the electrical conductivity of conductive particles filled polymer blends,” Colloid Polym. Sci. 270 134 139 1992 b) Levon K. Margolina A. Patashinsky A. Z. “Multiple percolation in conducting polymer blends,” Macromolecules 26 4061 4063 1993
- Ezquerra A. Martinez-Salazar J. Balta-Calleja F. J. “Conductive polyethylene-carbon black composites by elongational-flow injection molding,” J. Mater. Sci. Lett. 5 1065 1069 1986
- Medalia A. I. “Electrical conduction in carbon black composites” Rubber Chem. Tech. 59 432 454 1985
- Sumita M. Abe H. Kayaki H. Miyasaka K. J. Macromol. Sci.-Phys. B25 171 1986
- Bigg D. M. J. Rheol. 28 501 1984
- Geuskens G. Gielens J. L. Geshef D. Deltour R. “The electrical conductivity of polymer blends filled with carbon-black,” Eur. Polym. J. 23 993 995 1987
- Sumita M. Sakata K. Asai S. Miyasaka K. Nakagawa H. “Dispersion of fillers and the electrical conductivity of polymer blends filled with carbon black,” Polym. Bull. 25 265 271 1991
- Gubbels F. Blacher S. Vanlathem E. Jerome R. Deltour R. Brouers F. Teyssie Ph. “Design of electrical conductive composites: key role of the morphology on the electrical properties of carbon black filled polymer blends,” Macromolecules 28 1559 1566 1995
- Tchoudakov R. Breuer O. Narkis M. Siegmann A. “Conductive polymer blends with low carbon black loading: polypropylene/polyamide” Polymer Eng. Sci. 36 1336 1346 1996