Hydrogen Embrittlement in Automotive Fastener Applications
Annotation ability available
Sector:
Language:
English
Abstract
Fastener failure due to hydrogen embrittlement is of significant concern in the automotive industry. These types of failures occur unexpectedly. They may be very costly to the automotive company and fastener supplier, not only monetarily, but also in terms of customer satisfaction and safety. This paper is an overview of a program which one automotive company initiated to minimize hydrogen embrittlement in fasteners. The objectives of the program were two-fold. One was to obtain a better understanding of the hydrogen embrittlement phenomena as it relates to automotive fastener materials and processes. The second and most important objective, was to eliminate hydrogen embrittlement failures in vehicles.
Early program efforts concentrated on a review of fastener applications and corrosion protection systems to optimize coated fasteners for hydrogen embrittlement resistance. A concurrent program led to the development of a new fastener specification directed at minimizing hydrogen introduction and hydrogen retention as a result of coating application. Specific controls were put on fastener lot validation testing, and on baking practices as a function of fastener hardness level, cleaning and coating processes.
Joint research programs were initiated within academia and the fastener industry to better understand the fundamentals of hydrogen embrittlement in fasteners. The research program concentrated on the effects of hydrogen adsorption during electrochemical processing, hydrogen evolution during baking as functions of fastener-material and coating-process variation, and new multi-phase cold-heading steels. It is thought that these new steels may be inherently less susceptible to hydrogen damage than other commonly used fastener steel grades.
Recommended Content
Technical Paper | Poisoning of Zirconia Exhaust Oxygen Sensors by Silica |
Technical Paper | Use of Microfine Titanium Dioxide Pigment to Create Rayleigh Light Scattering in Automotive Coatings |
Technical Paper | Self-Piercing Rivets for Aluminum Components |
Authors
Topic
Citation
McCarty, E., Wetzel, D., and Kloberdanz, B., "Hydrogen Embrittlement in Automotive Fastener Applications," SAE Technical Paper 960312, 1996, https://doi.org/10.4271/960312.Also In
New Steel Products and Processing for Automotive Applications
Number: SP-1172; Published: 1996-02-01
Number: SP-1172; Published: 1996-02-01
References
- Johnson W.H. “On Some Remarkable Changes Produced in Iron and Steel by the Action of Hydrogen and Acids.” Hydrogen Damage Beachem C.D. American Society for Metals Metals Park, Ohio 1977 1 12
- Beachem C.D. Hydrogen Damage Beachem C.D. American Society for Metals Metals Park, Ohio 1977
- Coch L. “Plating Fasteners, Avoiding Embrittlement” Products Finishing May 1987 56 61
- “Hydrogen Embrittlement” Plating Systems and Technologies Bulletin Jackson, MI 1992
- Warren O. “Hydrogen Effects on Steel” Materials Performance January 1987 38 47
- Altmayer F. “From the Mailbox: Fastener Questions” Plating and Surface Finishing December 1991 35 36
- Shin K.S. Meshii M. “Effect of Sulfur Segregation and Hydrogen Charging on Intergranular Fracture of Iron” Perspectives in Hydrogen in Metals Ashby M.F. Hirth J.P. Pergamon Press New York 1986 693 700
- Thompson A. Bernstein I.M. “The Role Of Metallurgical Variables in Hydrogen-Assisted Environmental Fracture” Advances in Corrosion Science and Technology 7 Staehle R.W. Fontana M. Plenum Press 1979 53 75
- Costa J.E. Thompson A.W. “Effect of Hydrogen on Fracture Behavior of a Quenched and Tempered Medium-Carbon Steel” Metallurgical Transactions 12A May 1981 761 71
- Bernstein I.M. Garber R. Pressouyre G.M. Effects of Hydrogen on Behavior of Materials Thompson A.W. Bernstein I.M. TMS New York 1976 27 58
- Craig B.D. Krauss G. “The Structure of Tempered Martensite and its Susceptibility to Hydrogen Stress Cracking” Metallurgical Transactions 11A November 1980 1799 1807
- Bernstein I.M. Pressouyre G.M. “The Role of Traps in the Microstructural Control of Hydrogen Embrittlement of Steels” Hydrogen Degradation of Ferrous Alloys Oriani R.A. Hirth J.P. Smialowski M. Noyes Publications New Jersey 641 685
- Pressouyre G.M. “Trap Theory of Hydrogen Embrittlement” Act Metallurgica 28 1980 985 911
- Pressouyre G.M. “A Classification of Hydrogen Traps in Steel” Metallurgical Transactions 10A 1979 1571 1573
- Oriani R.A. “The Diffusion and Trapping of Hydrogen in Steel” Acta Metallurgica 18 1970 147 157
- Turnbull A. et al “Analysis of Hydrogen Diffusion and Trapping in a 13% Chromium Martensitic Stainless Steel” Acta Metallurgica 37 1989 2039 2046
- Grobin A.W. Jr. “Hydrogen Embrittlement Problems With Plated Fasteners and Other Hardware Items.” ASTM Standardization News March 1990 30 33
- Grobin A.W. Jr. “Hydrogen Embrittlement Problems with Plated Fasteners and Other Hardware Items (1) .” Metals Progress July 1990 71 73
- Troiano A.R. “The Role of Hydrogen and Other Interstitials in the Mechanical Behavior of Metals.” Hydrogen Damage Beachem C.D. American Society for Metals Metals Park, Ohio 1977 151 177
- “Standard Method for Mechanical Hydrogen Embrittlement Testing of Plating Processes and Aircraft Maintenance Chemicals” ASTM Designation F519-77, Annual Book of Standards 02.05 ASTM Philadelphia, PA 1989 760 770
- “Standard Test Methods for Determining the Mechanical Properties of Externally and Internally Threaded Fasteners, Washers, and Rivets,” ASTM Designation F606-86, Annual Book of Standards 15.08 ASTM Philadelphia, PA 1989 308
- “Standard Test Method for Measurement of Hydrogen Embrittlement in Steel by Incremental Loading Technique,” ASTM Designation F7.04 1996
- Smialowska Susan Rebak Raul Unpublished manuscript; Materials Engineering, Ohio State +University 1996