Impact Mechanism of Multiple Major Welding Parameters on Mechanical Properties of Laser Brazing Lap Joint of Galvanized Steel for Vehicle
Technical Paper
2017-01-5010
ISSN: 0148-7191, e-ISSN: 2688-3627
This content contains downloadable datasets
Annotation ability available
Sector:
Language:
English
Abstract
In order to research the effect of process parameters (laser power, welding speed, wire-feed speed, spot diameter) on mechanical properties of Zn-coated Steel Laser Brazing Lap Joint for vehicle, the influence of welding parameters on energy input of brazing seam cross section was theoretically analyzed, and then a great number of laser brazing experiments of 0.7mm galvanized steel was carried out. After that, the tensile strength and micro-hardness tests were also done for well-formed joints of galvanized steel formed in the laser brazing. The results show that joints with good mechanical properties and surface morphology can be formed when laser power is in the range of 2500-3200W and the other parameters keep in a specified range. Joint performance significantly reduces when the value of wire-feed speed exceeds 3.0m/min for that a wider brazing seam cross section can’t be formed. And tensile strength of the joint drops steeply when welding speed exceeds 50mm/s, because the solid-liquid surface tension between the brazing filler metal and the base metal increases. When the spot diameter increases within the appropriate range, the decrease of the energy density slows down the cooling rate of the brazing filler metal, which makes the mechanical properties of the brazing seam maintain a good condition. Moreover, under the same welding parameters, the micro-hardness anywhere inside the weld joint is uniform, which testifies the mechanical performance of the brazing seam is safe and stable.
Recommended Content
Technical Paper | Laser Hybrid Welding of Aluminized Coated Boron Steel for Automotive Body Construction |
Technical Paper | Laser Lap Welding of Galvanized Steel with No Gap |
Technical Paper | Tailor Welded Blank Technology for Automotive Applications |
Authors
Citation
Liu, H. and Zhang, X., "Impact Mechanism of Multiple Major Welding Parameters on Mechanical Properties of Laser Brazing Lap Joint of Galvanized Steel for Vehicle," SAE Technical Paper 2017-01-5010, 2017, https://doi.org/10.4271/2017-01-5010.Data Sets - Support Documents
Title | Description | Download |
---|---|---|
Unnamed Dataset 1 | ||
Unnamed Dataset 2 | ||
Unnamed Dataset 3 | ||
Unnamed Dataset 4 | ||
Unnamed Dataset 5 |
Also In
References
- Zhang , Y. , Li , S.C. , Jin , X.Z. et al Research on key technology of laser welding of galvanized steel Laser & Optoelectronics Progress 2010 07 33 41
- Li B. and Guo , L. Application of laser brazing in white body Society of Automotive Engineers of China 2013 3
- Lu , F.G. , Lu , B.F. and Tang , X.H. Study of influencing factors and joint performance of laser brazing on zinc- coated steel plate Int. J. Adv. Manuf. Technol. 2008 37 9- 10 961 965
- Feng , X.S. , Chen , Y.B. and Ni , J.M. Double beam laser brazing process Transactions of The China Welding Institution 2006 27 9 17 20
- Chen , Y.B. , Li , L.Q. and Zhou , S.B. Laser brazing of zinc-coated steel with filler wire Applied Laser 2004 06 357 360
- Reimann , W. , Dobler , M. and Goede , M. International Journal of Advanced Manufacturing Technology 2016 10.1007/s00170-016-9361-2
- Koltsov , A. , Bailly , N. and Cretteur , L. Wetting and laser brazing of Zn-coated steel products by Cu-Si filler metal Journal of Materials Science 2010 45 8 2118 2125
- Park , Y.W. , Yu , J. and Rhee , S. A Study on The Weld Characteristics of 5182 Aluminum Alloy by Nd:YAG Laser Welding With Filler Wire for Car Bodies International Journal of Automotive Technology 2010 11 5 729 736
- Lai , Z.M. , Zhang , L. and Wang , J.X. Influence of different filler metals on mechanical properties of laser brazing solder joint Transactions of The China Welding Institution 2011 12 85 88 117
- Ma , K. , Yu , Z.S. , Zhang , P.L. et al Effect of wire feeding speed on the properties of laser brazing joint of galvanized steel Chinese Journal of Lasers 2014 10 62 66
- Gu , Y.F. Study on the laser beam brazing process and defect inhibition mechanism of galvanized steel Huazhong University of Science and Technology 2014