Laminated Composite of Sisal and Curaua Fibers to Different Settings for Use in Bumper Cars
Technical Paper
2013-36-0603
ISSN: 0148-7191, e-ISSN: 2688-3627
Annotation ability available
Sector:
Language:
English
Abstract
The use of composite materials reinforced with natural fibers has been widely studied in recent research seen the availability of feedstock and mainly because the productions facility, low cost and because they are biodegradable. In order to expand the applications of composite materials, this paper proposed to develop hybrid laminar composites associating natural fibers as jute, sisal and curaua in an array of type resin polyester and compare them with commercial bumpers available on the market. The sisal and curaua fibers were manually cut into lengths of 50 mm and then were arranged and incorporated separately with the polyester resin and the jute fiber cut, as a blanket in length 400 × 400 mm2 adopting for that a simple and manual manufacture process. Finally, it was executed a tensile test in hybrid laminated, and then a comparative study of tensile properties of different laminated hybrid composites, jute-sisal, jute-curaua and between the results of the commercial bumpers. The results showed the sisal-jute composite was better because this hybrid laminated had more satisfactory tensile strength and elongation than others.
Authors
- Lírian Said de Lima - Universidade Federal do Pará
- César Tadeu Nasser Medeiros Branco - Universidade Federal do Pará
- Rodrigo Maurício Costa dos Santos - Universidade Federal do Pará
- Frank Valdo Monteiro de Lima - Universidade Federal do Pará
- Deibson Silva da Costa - Universidade Federal do Pará
- Wassim Raja El Banna - Universidade Federal do Pará
- Roberto Tetsuo Fujiyama - Universidade Federal do Pará
Topic
Citation
de Lima, L., Branco, C., Costa dos Santos, R., de Lima, F. et al., "Laminated Composite of Sisal and Curaua Fibers to Different Settings for Use in Bumper Cars," SAE Technical Paper 2013-36-0603, 2013, https://doi.org/10.4271/2013-36-0603.Also In
References
- Gianluca , C. , Giuseppe C. , Giuseppe R. , Alberta L. Composites Based on Natural Fibre Fabrics, Woven Fabric Engineering University Campus STeP Ri: InTech 2010 http://www.intechopen.com/books/woven-fabric-engineering/composites-based-on-naturalfibre-Fabrics 20 Fev 2013
- Joseph , K. , Medeiros , Eliton. , Carvalho , Laura Compósitos de Matriz Poliéster Reforçados por Fibras Curtas de Sisal Universidade Federal da Paraíba: Technical Scientific Article 1999 www.scielo.br/pdf/po/v9n4/6195.pdf 10 Apr 2013
- Monteiro , S. , Aquino , R. , Lopes , F. , Carvalho , E. et al. Comportamento mecânico e características estruturais de compósitos poliméricos reforçados com fibras contínuas e alinhadas de curauá Rio de Janeiro 11 3 Sept. 2006 http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1517-70762006000300005&lng=en&nrm==iso 27 May 2013
- Pematec Triangel http://www.pematec.com.br/curaua.htm 23 Fev. 2013
- Rodrigues , J. da S. Comportamento Mecânico de Material Compósito de Matriz Poliéster Reforçado por Sistema Híbrido Fibras Naturais e Resíduos da Indústria Madeireira Universidade Federal do Pará Belém 2008 91 f Dissertation (Master's degree in Mechanical Engineering)
- Takahashi , R. Desenvolvimento de material compósito de matriz polimérica reforçada a partir de pré-pregs de fibras naturais de curauá e sisal Universidade Federal do Pará Belém 2011 54 Thesis (Completion of Course Work)
- ASTM D 3822 - 96 Standard Test Method for Tensile Properties of Single Textile Fibers Annual Book of ASTM Standards American Society for Testing and Materials
- Departamento Nacional de Estradas e Rodagem 1995 DNER-ME 084/95 Agregado miúdo - determinação da densidade real
- ASTM D3039 Standard Test Method for Tensile Properties of Polymer Matrix Composite Materials Annual Book of ASTM Standards American Society for Testing and Materials
- Fernandes , B. , Domingues , Antonio Caracterização Mecânica de Polipropileno Reciclado para a Indústria Automotiva PUC, Paraná Technical Scientific Article www.scielo.br/pdf/po/v17n2/a05v17n2.pdf 10 May 2013